N08332 Stainless Steel vs. SAE-AISI M30 Steel

Both N08332 stainless steel and SAE-AISI M30 steel are iron alloys. They have 48% of their average alloy composition in common. There are 22 material properties with values for both materials. Properties with values for just one material (12, in this case) are not shown.

For each property being compared, the top bar is N08332 stainless steel and the bottom bar is SAE-AISI M30 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
200
Poisson's Ratio 0.28
0.29
Shear Modulus, GPa 76
78
Tensile Strength: Ultimate (UTS), MPa 520
800 to 2170

Thermal Properties

Latent Heat of Fusion, J/g 310
270
Melting Completion (Liquidus), °C 1390
1550
Melting Onset (Solidus), °C 1340
1500
Specific Heat Capacity, J/kg-K 480
450
Thermal Conductivity, W/m-K 12
24
Thermal Expansion, µm/m-K 16
12

Otherwise Unclassified Properties

Base Metal Price, % relative 32
26
Density, g/cm3 8.0
8.2
Embodied Carbon, kg CO2/kg material 5.4
7.2
Embodied Energy, MJ/kg 77
100
Embodied Water, L/kg 190
120

Common Calculations

PREN (Pitting Resistance) 19
35
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 24
24
Strength to Weight: Axial, points 18
27 to 74
Strength to Weight: Bending, points 18
24 to 46
Thermal Diffusivity, mm2/s 3.1
6.6
Thermal Shock Resistance, points 12
25 to 67

Alloy Composition

Carbon (C), % 0.050 to 0.1
0.75 to 0.85
Chromium (Cr), % 17 to 20
3.5 to 4.3
Cobalt (Co), % 0
4.5 to 5.5
Copper (Cu), % 0 to 1.0
0 to 0.25
Iron (Fe), % 38.3 to 48.2
75.2 to 80.9
Lead (Pb), % 0 to 0.0050
0
Manganese (Mn), % 0 to 2.0
0.15 to 0.4
Molybdenum (Mo), % 0
7.8 to 9.0
Nickel (Ni), % 34 to 37
0 to 0.3
Phosphorus (P), % 0 to 0.030
0 to 0.030
Silicon (Si), % 0.75 to 1.5
0.2 to 0.45
Sulfur (S), % 0 to 0.030
0 to 0.030
Tin (Sn), % 0 to 0.025
0
Tungsten (W), % 0
1.3 to 2.3
Vanadium (V), % 0
1.0 to 1.4