N08332 Stainless Steel vs. SAE-AISI T1 Steel

Both N08332 stainless steel and SAE-AISI T1 steel are iron alloys. They have 48% of their average alloy composition in common. There are 22 material properties with values for both materials. Properties with values for just one material (12, in this case) are not shown.

For each property being compared, the top bar is N08332 stainless steel and the bottom bar is SAE-AISI T1 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
200
Poisson's Ratio 0.28
0.29
Shear Modulus, GPa 76
80
Tensile Strength: Ultimate (UTS), MPa 520
770 to 2130

Thermal Properties

Latent Heat of Fusion, J/g 310
240
Melting Completion (Liquidus), °C 1390
1810
Melting Onset (Solidus), °C 1340
1750
Specific Heat Capacity, J/kg-K 480
410
Thermal Conductivity, W/m-K 12
20
Thermal Expansion, µm/m-K 16
12

Otherwise Unclassified Properties

Base Metal Price, % relative 32
45
Density, g/cm3 8.0
9.3
Embodied Carbon, kg CO2/kg material 5.4
8.2
Embodied Energy, MJ/kg 77
130
Embodied Water, L/kg 190
90

Common Calculations

PREN (Pitting Resistance) 19
34
Stiffness to Weight: Axial, points 14
12
Stiffness to Weight: Bending, points 24
21
Strength to Weight: Axial, points 18
23 to 64
Strength to Weight: Bending, points 18
20 to 40
Thermal Diffusivity, mm2/s 3.1
5.2
Thermal Shock Resistance, points 12
23 to 64

Alloy Composition

Carbon (C), % 0.050 to 0.1
0.65 to 0.8
Chromium (Cr), % 17 to 20
3.8 to 4.5
Copper (Cu), % 0 to 1.0
0 to 0.25
Iron (Fe), % 38.3 to 48.2
73.2 to 77.2
Lead (Pb), % 0 to 0.0050
0
Manganese (Mn), % 0 to 2.0
0.1 to 0.4
Nickel (Ni), % 34 to 37
0 to 0.3
Phosphorus (P), % 0 to 0.030
0 to 0.030
Silicon (Si), % 0.75 to 1.5
0.2 to 0.4
Sulfur (S), % 0 to 0.030
0 to 0.030
Tin (Sn), % 0 to 0.025
0
Tungsten (W), % 0
17.3 to 18.8
Vanadium (V), % 0
0.9 to 1.3