N08535 Stainless Steel vs. ASTM A202 Steel

Both N08535 stainless steel and ASTM A202 steel are iron alloys. There are 30 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown.

For each property being compared, the top bar is N08535 stainless steel and the bottom bar is ASTM A202 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
190
Elongation at Break, % 46
17 to 18
Fatigue Strength, MPa 220
240
Poisson's Ratio 0.28
0.29
Shear Modulus, GPa 80
73
Shear Strength, MPa 400
360 to 410
Tensile Strength: Ultimate (UTS), MPa 570
590 to 670
Tensile Strength: Yield (Proof), MPa 240
350 to 360

Thermal Properties

Latent Heat of Fusion, J/g 310
260
Maximum Temperature: Mechanical, °C 1100
410
Melting Completion (Liquidus), °C 1420
1450
Melting Onset (Solidus), °C 1370
1410
Specific Heat Capacity, J/kg-K 470
470
Thermal Conductivity, W/m-K 13
52
Thermal Expansion, µm/m-K 16
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 1.7
7.3
Electrical Conductivity: Equal Weight (Specific), % IACS 1.9
8.4

Otherwise Unclassified Properties

Base Metal Price, % relative 36
2.1
Density, g/cm3 8.1
7.8
Embodied Carbon, kg CO2/kg material 6.3
1.4
Embodied Energy, MJ/kg 87
19
Embodied Water, L/kg 230
49

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 210
93 to 96
Resilience: Unit (Modulus of Resilience), kJ/m3 140
330 to 350
Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 24
24
Strength to Weight: Axial, points 20
21 to 24
Strength to Weight: Bending, points 19
20 to 22
Thermal Diffusivity, mm2/s 3.3
14
Thermal Shock Resistance, points 13
17 to 20