N08700 Stainless Steel vs. EN 1.1061 Steel

Both N08700 stainless steel and EN 1.1061 steel are iron alloys. They have 48% of their average alloy composition in common. There are 25 material properties with values for both materials. Properties with values for just one material (10, in this case) are not shown.

For each property being compared, the top bar is N08700 stainless steel and the bottom bar is EN 1.1061 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 170
150 to 180
Elastic (Young's, Tensile) Modulus, GPa 200
190
Poisson's Ratio 0.28
0.29
Shear Modulus, GPa 79
72
Tensile Strength: Ultimate (UTS), MPa 620
530 to 1810

Thermal Properties

Latent Heat of Fusion, J/g 300
250
Maximum Temperature: Mechanical, °C 1100
400
Melting Completion (Liquidus), °C 1450
1460
Melting Onset (Solidus), °C 1400
1420
Specific Heat Capacity, J/kg-K 470
470
Thermal Conductivity, W/m-K 13
51
Thermal Expansion, µm/m-K 16
12

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 1.7
7.1
Electrical Conductivity: Equal Weight (Specific), % IACS 1.9
8.1

Otherwise Unclassified Properties

Base Metal Price, % relative 32
1.8
Density, g/cm3 8.1
7.8
Embodied Carbon, kg CO2/kg material 6.0
1.4
Embodied Energy, MJ/kg 82
19
Embodied Water, L/kg 200
46

Common Calculations

Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 24
24
Strength to Weight: Axial, points 21
19 to 64
Strength to Weight: Bending, points 20
19 to 42
Thermal Diffusivity, mm2/s 3.5
14
Thermal Shock Resistance, points 14
17 to 58

Alloy Composition

Carbon (C), % 0 to 0.040
0.42 to 0.5
Chromium (Cr), % 19 to 23
0
Copper (Cu), % 0 to 0.5
0 to 0.25
Iron (Fe), % 42 to 52.7
98.1 to 99.06
Manganese (Mn), % 0 to 2.0
0.5 to 0.8
Molybdenum (Mo), % 4.3 to 5.0
0
Nickel (Ni), % 24 to 26
0
Niobium (Nb), % 0 to 0.4
0
Phosphorus (P), % 0 to 0.040
0 to 0.025
Silicon (Si), % 0 to 1.0
0 to 0.3
Sulfur (S), % 0 to 0.030
0.020 to 0.035