N08800 Stainless Steel vs. C46500 Brass
N08800 stainless steel belongs to the iron alloys classification, while C46500 brass belongs to the copper alloys. There are 29 material properties with values for both materials. Properties with values for just one material (6, in this case) are not shown.
For each property being compared, the top bar is N08800 stainless steel and the bottom bar is C46500 brass.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 200 | |
| 100 |
| Elongation at Break, % | 4.5 to 34 | |
| 18 to 50 |
| Poisson's Ratio | 0.28 | |
| 0.31 |
| Shear Modulus, GPa | 77 | |
| 40 |
| Shear Strength, MPa | 340 to 580 | |
| 280 to 380 |
| Tensile Strength: Ultimate (UTS), MPa | 500 to 1000 | |
| 380 to 610 |
| Tensile Strength: Yield (Proof), MPa | 190 to 830 | |
| 190 to 490 |
Thermal Properties
| Latent Heat of Fusion, J/g | 300 | |
| 170 |
| Maximum Temperature: Mechanical, °C | 1100 | |
| 120 |
| Melting Completion (Liquidus), °C | 1390 | |
| 900 |
| Melting Onset (Solidus), °C | 1360 | |
| 890 |
| Specific Heat Capacity, J/kg-K | 480 | |
| 380 |
| Thermal Conductivity, W/m-K | 12 | |
| 120 |
| Thermal Expansion, µm/m-K | 14 | |
| 21 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 1.7 | |
| 26 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 1.9 | |
| 29 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 30 | |
| 23 |
| Density, g/cm3 | 8.0 | |
| 8.0 |
| Embodied Carbon, kg CO2/kg material | 5.3 | |
| 2.7 |
| Embodied Energy, MJ/kg | 76 | |
| 47 |
| Embodied Water, L/kg | 200 | |
| 330 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 42 to 160 | |
| 99 to 160 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 96 to 1740 | |
| 170 to 1170 |
| Stiffness to Weight: Axial, points | 14 | |
| 7.2 |
| Stiffness to Weight: Bending, points | 24 | |
| 20 |
| Strength to Weight: Axial, points | 18 to 35 | |
| 13 to 21 |
| Strength to Weight: Bending, points | 18 to 28 | |
| 15 to 20 |
| Thermal Diffusivity, mm2/s | 3.0 | |
| 38 |
| Thermal Shock Resistance, points | 13 to 25 | |
| 13 to 20 |
Alloy Composition
Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 460
| Aluminum (Al), % | 0.15 to 0.6 | |
| 0 |
| Arsenic (As), % | 0 | |
| 0.020 to 0.060 |
| Carbon (C), % | 0 to 0.1 | |
| 0 |
| Chromium (Cr), % | 19 to 23 | |
| 0 |
| Copper (Cu), % | 0 to 0.75 | |
| 59 to 62 |
| Iron (Fe), % | 39.5 to 50.7 | |
| 0 to 0.1 |
| Lead (Pb), % | 0 | |
| 0 to 0.2 |
| Manganese (Mn), % | 0 to 1.5 | |
| 0 |
| Nickel (Ni), % | 30 to 35 | |
| 0 |
| Phosphorus (P), % | 0 to 0.045 | |
| 0 |
| Silicon (Si), % | 0 to 1.0 | |
| 0 |
| Sulfur (S), % | 0 to 0.015 | |
| 0 |
| Tin (Sn), % | 0 | |
| 0.5 to 1.0 |
| Titanium (Ti), % | 0.15 to 0.6 | |
| 0 |
| Zinc (Zn), % | 0 | |
| 36.2 to 40.5 |
| Residuals, % | 0 | |
| 0 to 0.4 |