N08801 Stainless Steel vs. Z13004 Zinc

N08801 stainless steel belongs to the iron alloys classification, while Z13004 zinc belongs to the zinc alloys. There are 28 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown.

For each property being compared, the top bar is N08801 stainless steel and the bottom bar is Z13004 zinc.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
87
Elongation at Break, % 34
30
Poisson's Ratio 0.28
0.25
Shear Modulus, GPa 77
35
Tensile Strength: Ultimate (UTS), MPa 860
93
Tensile Strength: Yield (Proof), MPa 190
76

Thermal Properties

Latent Heat of Fusion, J/g 300
110
Maximum Temperature: Mechanical, °C 1090
90
Melting Completion (Liquidus), °C 1390
410
Melting Onset (Solidus), °C 1360
390
Specific Heat Capacity, J/kg-K 480
390
Thermal Conductivity, W/m-K 12
110
Thermal Expansion, µm/m-K 16
26

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 1.7
27
Electrical Conductivity: Equal Weight (Specific), % IACS 1.9
37

Otherwise Unclassified Properties

Base Metal Price, % relative 30
11
Density, g/cm3 8.0
6.6
Embodied Carbon, kg CO2/kg material 5.5
2.8
Embodied Energy, MJ/kg 79
53
Embodied Water, L/kg 200
340

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 220
26
Resilience: Unit (Modulus of Resilience), kJ/m3 92
33
Stiffness to Weight: Axial, points 14
7.4
Stiffness to Weight: Bending, points 24
23
Strength to Weight: Axial, points 30
3.9
Strength to Weight: Bending, points 25
7.0
Thermal Diffusivity, mm2/s 3.3
44
Thermal Shock Resistance, points 20
2.9

Alloy Composition

Aluminum (Al), % 0
0 to 0.0020
Cadmium (Cd), % 0
0 to 0.0030
Carbon (C), % 0 to 0.1
0
Chromium (Cr), % 19 to 22
0
Copper (Cu), % 0 to 0.5
0 to 0.0030
Iron (Fe), % 39.5 to 50.3
0 to 0.0030
Lead (Pb), % 0
0 to 0.0030
Manganese (Mn), % 0 to 1.5
0
Nickel (Ni), % 30 to 34
0
Silicon (Si), % 0 to 1.0
0
Sulfur (S), % 0 to 0.015
0
Tin (Sn), % 0
0 to 0.0010
Titanium (Ti), % 0.75 to 1.5
0
Zinc (Zn), % 0
99.985 to 100