N08810 Stainless Steel vs. S30600 Stainless Steel

Both N08810 stainless steel and S30600 stainless steel are iron alloys. Both are furnished in the annealed condition. They have 79% of their average alloy composition in common. There are 32 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown.

For each property being compared, the top bar is N08810 stainless steel and the bottom bar is S30600 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
190
Elongation at Break, % 33
45
Fatigue Strength, MPa 160
250
Poisson's Ratio 0.28
0.28
Shear Modulus, GPa 77
76
Shear Strength, MPa 340
430
Tensile Strength: Ultimate (UTS), MPa 520
610
Tensile Strength: Yield (Proof), MPa 200
270

Thermal Properties

Latent Heat of Fusion, J/g 300
350
Maximum Temperature: Corrosion, °C 490
410
Maximum Temperature: Mechanical, °C 1100
950
Melting Completion (Liquidus), °C 1400
1380
Melting Onset (Solidus), °C 1350
1330
Specific Heat Capacity, J/kg-K 480
490
Thermal Conductivity, W/m-K 12
14
Thermal Expansion, µm/m-K 14
16

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 1.7
2.1
Electrical Conductivity: Equal Weight (Specific), % IACS 1.9
2.5

Otherwise Unclassified Properties

Base Metal Price, % relative 30
19
Density, g/cm3 8.0
7.6
Embodied Carbon, kg CO2/kg material 5.3
3.6
Embodied Energy, MJ/kg 76
51
Embodied Water, L/kg 200
150

Common Calculations

PREN (Pitting Resistance) 21
18
Resilience: Ultimate (Unit Rupture Work), MJ/m3 140
220
Resilience: Unit (Modulus of Resilience), kJ/m3 100
190
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 24
25
Strength to Weight: Axial, points 18
22
Strength to Weight: Bending, points 18
21
Thermal Diffusivity, mm2/s 3.0
3.7
Thermal Shock Resistance, points 13
14

Alloy Composition

Aluminum (Al), % 0.15 to 0.6
0
Carbon (C), % 0.050 to 0.1
0 to 0.018
Chromium (Cr), % 19 to 23
17 to 18.5
Copper (Cu), % 0 to 0.75
0 to 0.5
Iron (Fe), % 39.5 to 50.7
58.9 to 65.3
Manganese (Mn), % 0 to 1.5
0 to 2.0
Molybdenum (Mo), % 0
0 to 0.2
Nickel (Ni), % 30 to 35
14 to 15.5
Phosphorus (P), % 0 to 0.045
0 to 0.020
Silicon (Si), % 0 to 1.0
3.7 to 4.3
Sulfur (S), % 0 to 0.015
0 to 0.020
Titanium (Ti), % 0.15 to 0.6
0