R05400 Tantalum vs. EN 1.8936 Steel

R05400 tantalum belongs to the otherwise unclassified metals classification, while EN 1.8936 steel belongs to the iron alloys. There are 20 material properties with values for both materials. Properties with values for just one material (11, in this case) are not shown. Please note that the two materials have significantly dissimilar densities. This means that additional care is required when interpreting the data, because some material properties are based on units of mass, while others are based on units of area or volume.

For each property being compared, the top bar is R05400 tantalum and the bottom bar is EN 1.8936 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
190
Elongation at Break, % 1.1 to 28
20
Poisson's Ratio 0.34
0.29
Shear Modulus, GPa 69
73
Tensile Strength: Ultimate (UTS), MPa 210 to 540
600
Tensile Strength: Yield (Proof), MPa 140 to 390
370

Thermal Properties

Latent Heat of Fusion, J/g 140
250
Specific Heat Capacity, J/kg-K 140
470
Thermal Conductivity, W/m-K 59
40
Thermal Expansion, µm/m-K 6.5
13

Otherwise Unclassified Properties

Density, g/cm3 17
7.8
Embodied Water, L/kg 650
50

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 5.5 to 53
100
Resilience: Unit (Modulus of Resilience), kJ/m3 50 to 420
370
Stiffness to Weight: Axial, points 6.2
13
Stiffness to Weight: Bending, points 11
24
Strength to Weight: Axial, points 3.6 to 9.0
21
Strength to Weight: Bending, points 4.8 to 8.8
20
Thermal Diffusivity, mm2/s 25
11
Thermal Shock Resistance, points 13 to 32
17

Alloy Composition

Aluminum (Al), % 0
0 to 0.060
Carbon (C), % 0 to 0.010
0 to 0.2
Chromium (Cr), % 0
0 to 0.3
Copper (Cu), % 0
0 to 0.2
Hydrogen (H), % 0 to 0.0015
0
Iron (Fe), % 0 to 0.010
95.5 to 98.9
Manganese (Mn), % 0
1.0 to 1.7
Molybdenum (Mo), % 0 to 0.020
0 to 0.1
Nickel (Ni), % 0 to 0.010
0 to 1.0
Niobium (Nb), % 0 to 0.1
0 to 0.050
Nitrogen (N), % 0 to 0.010
0 to 0.020
Oxygen (O), % 0 to 0.030
0
Phosphorus (P), % 0
0 to 0.025
Silicon (Si), % 0 to 0.0050
0.1 to 0.6
Sulfur (S), % 0
0 to 0.015
Tantalum (Ta), % 99.7 to 100
0
Titanium (Ti), % 0 to 0.010
0
Tungsten (W), % 0 to 0.050
0
Vanadium (V), % 0
0 to 0.2