R30021 Cobalt vs. S32001 Stainless Steel

R30021 cobalt belongs to the cobalt alloys classification, while S32001 stainless steel belongs to the iron alloys. They have a modest 25% of their average alloy composition in common, which, by itself, doesn't mean much. There are 28 material properties with values for both materials. Properties with values for just one material (6, in this case) are not shown.

For each property being compared, the top bar is R30021 cobalt and the bottom bar is S32001 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 220
200
Elongation at Break, % 9.0
28
Fatigue Strength, MPa 250
370
Poisson's Ratio 0.29
0.28
Rockwell C Hardness 32
22
Shear Modulus, GPa 86
78
Tensile Strength: Ultimate (UTS), MPa 700
690
Tensile Strength: Yield (Proof), MPa 500
510

Thermal Properties

Latent Heat of Fusion, J/g 330
290
Melting Completion (Liquidus), °C 1350
1420
Melting Onset (Solidus), °C 1190
1370
Specific Heat Capacity, J/kg-K 450
480
Thermal Conductivity, W/m-K 15
15
Thermal Expansion, µm/m-K 11
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 1.9
2.2
Electrical Conductivity: Equal Weight (Specific), % IACS 2.1
2.6

Otherwise Unclassified Properties

Density, g/cm3 8.4
7.7
Embodied Carbon, kg CO2/kg material 8.0
2.6
Embodied Energy, MJ/kg 110
37
Embodied Water, L/kg 520
150

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 57
180
Resilience: Unit (Modulus of Resilience), kJ/m3 570
660
Stiffness to Weight: Axial, points 15
14
Stiffness to Weight: Bending, points 24
25
Strength to Weight: Axial, points 23
25
Strength to Weight: Bending, points 21
23
Thermal Diffusivity, mm2/s 3.8
4.0
Thermal Shock Resistance, points 21
19

Alloy Composition

Carbon (C), % 0.2 to 0.35
0 to 0.030
Chromium (Cr), % 26 to 29
19.5 to 21.5
Cobalt (Co), % 61.7 to 67.3
0
Copper (Cu), % 0
0 to 1.0
Iron (Fe), % 0 to 3.0
66.6 to 75.5
Manganese (Mn), % 0
4.0 to 6.0
Molybdenum (Mo), % 4.5 to 6.0
0 to 0.6
Nickel (Ni), % 2.0 to 3.0
1.0 to 3.0
Nitrogen (N), % 0
0.050 to 0.17
Phosphorus (P), % 0
0 to 0.040
Silicon (Si), % 0 to 1.5
0 to 1.0
Sulfur (S), % 0
0 to 0.030