R30035 Cobalt vs. AISI 414 Stainless Steel
R30035 cobalt belongs to the cobalt alloys classification, while AISI 414 stainless steel belongs to the iron alloys. There are 29 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown.
For each property being compared, the top bar is R30035 cobalt and the bottom bar is AISI 414 stainless steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 220 to 230 | |
| 190 |
| Elongation at Break, % | 9.0 to 46 | |
| 17 |
| Fatigue Strength, MPa | 170 to 740 | |
| 430 to 480 |
| Poisson's Ratio | 0.29 | |
| 0.28 |
| Reduction in Area, % | 40 to 74 | |
| 50 |
| Shear Modulus, GPa | 84 to 89 | |
| 76 |
| Tensile Strength: Ultimate (UTS), MPa | 900 to 1900 | |
| 900 to 960 |
| Tensile Strength: Yield (Proof), MPa | 300 to 1650 | |
| 700 to 790 |
Thermal Properties
| Latent Heat of Fusion, J/g | 320 | |
| 280 |
| Melting Completion (Liquidus), °C | 1440 | |
| 1440 |
| Melting Onset (Solidus), °C | 1320 | |
| 1400 |
| Specific Heat Capacity, J/kg-K | 440 | |
| 480 |
| Thermal Conductivity, W/m-K | 11 | |
| 25 |
| Thermal Expansion, µm/m-K | 13 | |
| 10 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 1.7 | |
| 2.5 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 1.8 | |
| 2.9 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 100 | |
| 8.0 |
| Density, g/cm3 | 8.7 | |
| 7.8 |
| Embodied Carbon, kg CO2/kg material | 10 | |
| 2.1 |
| Embodied Energy, MJ/kg | 140 | |
| 29 |
| Embodied Water, L/kg | 410 | |
| 100 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 160 to 320 | |
| 140 to 150 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 210 to 5920 | |
| 1260 to 1590 |
| Stiffness to Weight: Axial, points | 14 to 15 | |
| 14 |
| Stiffness to Weight: Bending, points | 23 to 24 | |
| 25 |
| Strength to Weight: Axial, points | 29 to 61 | |
| 32 to 34 |
| Strength to Weight: Bending, points | 24 to 39 | |
| 27 to 28 |
| Thermal Diffusivity, mm2/s | 3.0 | |
| 6.7 |
| Thermal Shock Resistance, points | 23 to 46 | |
| 33 to 35 |
Alloy Composition
| Boron (B), % | 0 to 0.015 | |
| 0 |
| Carbon (C), % | 0 to 0.025 | |
| 0 to 0.15 |
| Chromium (Cr), % | 19 to 21 | |
| 11.5 to 13.5 |
| Cobalt (Co), % | 29.1 to 39 | |
| 0 |
| Iron (Fe), % | 0 to 1.0 | |
| 81.8 to 87.3 |
| Manganese (Mn), % | 0 to 0.15 | |
| 0 to 1.0 |
| Molybdenum (Mo), % | 9.0 to 10.5 | |
| 0 |
| Nickel (Ni), % | 33 to 37 | |
| 1.3 to 2.5 |
| Phosphorus (P), % | 0 to 0.015 | |
| 0 to 0.040 |
| Silicon (Si), % | 0 to 0.15 | |
| 0 to 1.0 |
| Sulfur (S), % | 0 to 0.010 | |
| 0 to 0.030 |
| Titanium (Ti), % | 0 to 1.0 | |
| 0 |