R30556 Alloy vs. ASTM A369 Grade FP91
Both R30556 alloy and ASTM A369 grade FP91 are iron alloys. They have 40% of their average alloy composition in common. There are 31 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown.
For each property being compared, the top bar is R30556 alloy and the bottom bar is ASTM A369 grade FP91.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 210 | |
| 190 |
| Elongation at Break, % | 45 | |
| 19 |
| Fatigue Strength, MPa | 320 | |
| 320 |
| Poisson's Ratio | 0.28 | |
| 0.28 |
| Shear Modulus, GPa | 81 | |
| 75 |
| Shear Strength, MPa | 550 | |
| 410 |
| Tensile Strength: Ultimate (UTS), MPa | 780 | |
| 670 |
| Tensile Strength: Yield (Proof), MPa | 350 | |
| 460 |
Thermal Properties
| Latent Heat of Fusion, J/g | 300 | |
| 270 |
| Maximum Temperature: Mechanical, °C | 1100 | |
| 600 |
| Melting Completion (Liquidus), °C | 1420 | |
| 1460 |
| Melting Onset (Solidus), °C | 1330 | |
| 1420 |
| Specific Heat Capacity, J/kg-K | 450 | |
| 470 |
| Thermal Conductivity, W/m-K | 11 | |
| 26 |
| Thermal Expansion, µm/m-K | 15 | |
| 13 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 1.8 | |
| 8.9 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 1.9 | |
| 10 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 70 | |
| 7.0 |
| Density, g/cm3 | 8.4 | |
| 7.8 |
| Embodied Carbon, kg CO2/kg material | 8.7 | |
| 2.6 |
| Embodied Energy, MJ/kg | 130 | |
| 37 |
| Embodied Water, L/kg | 300 | |
| 88 |
Common Calculations
| PREN (Pitting Resistance) | 40 | |
| 13 |
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 290 | |
| 110 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 290 | |
| 560 |
| Stiffness to Weight: Axial, points | 14 | |
| 14 |
| Stiffness to Weight: Bending, points | 23 | |
| 25 |
| Strength to Weight: Axial, points | 26 | |
| 24 |
| Strength to Weight: Bending, points | 22 | |
| 22 |
| Thermal Diffusivity, mm2/s | 2.9 | |
| 6.9 |
| Thermal Shock Resistance, points | 18 | |
| 18 |
Alloy Composition
| Aluminum (Al), % | 0.1 to 0.5 | |
| 0 to 0.020 |
| Boron (B), % | 0 to 0.020 | |
| 0 |
| Carbon (C), % | 0.050 to 0.15 | |
| 0.080 to 0.12 |
| Chromium (Cr), % | 21 to 23 | |
| 8.0 to 9.5 |
| Cobalt (Co), % | 16 to 21 | |
| 0 |
| Iron (Fe), % | 20.4 to 38.2 | |
| 87.3 to 90.3 |
| Lanthanum (La), % | 0.0050 to 0.1 | |
| 0 |
| Manganese (Mn), % | 0.5 to 2.0 | |
| 0.3 to 0.6 |
| Molybdenum (Mo), % | 2.5 to 4.0 | |
| 0.85 to 1.1 |
| Nickel (Ni), % | 19 to 22.5 | |
| 0 to 0.4 |
| Niobium (Nb), % | 0 to 0.3 | |
| 0.060 to 0.1 |
| Nitrogen (N), % | 0.1 to 0.3 | |
| 0.030 to 0.070 |
| Phosphorus (P), % | 0 to 0.040 | |
| 0 to 0.025 |
| Silicon (Si), % | 0.2 to 0.8 | |
| 0.2 to 0.5 |
| Sulfur (S), % | 0 to 0.015 | |
| 0 to 0.025 |
| Tantalum (Ta), % | 0.3 to 1.3 | |
| 0 |
| Titanium (Ti), % | 0 | |
| 0 to 0.010 |
| Tungsten (W), % | 2.0 to 3.5 | |
| 0 |
| Vanadium (V), % | 0 | |
| 0.18 to 0.25 |
| Zinc (Zn), % | 0.0010 to 0.1 | |
| 0 |
| Zirconium (Zr), % | 0 | |
| 0 to 0.010 |