R30556 Alloy vs. AWS ERNiCrMo-2
R30556 alloy belongs to the iron alloys classification, while AWS ERNiCrMo-2 belongs to the nickel alloys. They have 67% of their average alloy composition in common. There are 23 material properties with values for both materials. Properties with values for just one material (9, in this case) are not shown.
For each property being compared, the top bar is R30556 alloy and the bottom bar is AWS ERNiCrMo-2.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 210 | |
| 210 |
| Poisson's Ratio | 0.28 | |
| 0.28 |
| Shear Modulus, GPa | 81 | |
| 81 |
| Tensile Strength: Ultimate (UTS), MPa | 780 | |
| 750 |
Thermal Properties
| Latent Heat of Fusion, J/g | 300 | |
| 320 |
| Melting Completion (Liquidus), °C | 1420 | |
| 1460 |
| Melting Onset (Solidus), °C | 1330 | |
| 1410 |
| Specific Heat Capacity, J/kg-K | 450 | |
| 450 |
| Thermal Conductivity, W/m-K | 11 | |
| 11 |
| Thermal Expansion, µm/m-K | 15 | |
| 13 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 1.8 | |
| 1.5 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 1.9 | |
| 1.6 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 70 | |
| 55 |
| Density, g/cm3 | 8.4 | |
| 8.4 |
| Embodied Carbon, kg CO2/kg material | 8.7 | |
| 9.2 |
| Embodied Energy, MJ/kg | 130 | |
| 120 |
| Embodied Water, L/kg | 300 | |
| 270 |
Common Calculations
| Stiffness to Weight: Axial, points | 14 | |
| 14 |
| Stiffness to Weight: Bending, points | 23 | |
| 23 |
| Strength to Weight: Axial, points | 26 | |
| 25 |
| Strength to Weight: Bending, points | 22 | |
| 22 |
| Thermal Diffusivity, mm2/s | 2.9 | |
| 2.9 |
| Thermal Shock Resistance, points | 18 | |
| 20 |
Alloy Composition
Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 460
| Aluminum (Al), % | 0.1 to 0.5 | |
| 0 |
| Boron (B), % | 0 to 0.020 | |
| 0 |
| Carbon (C), % | 0.050 to 0.15 | |
| 0.050 to 0.15 |
| Chromium (Cr), % | 21 to 23 | |
| 20.5 to 23 |
| Cobalt (Co), % | 16 to 21 | |
| 0.5 to 2.5 |
| Copper (Cu), % | 0 | |
| 0 to 0.5 |
| Iron (Fe), % | 20.4 to 38.2 | |
| 17 to 20 |
| Lanthanum (La), % | 0.0050 to 0.1 | |
| 0 |
| Manganese (Mn), % | 0.5 to 2.0 | |
| 0 to 1.0 |
| Molybdenum (Mo), % | 2.5 to 4.0 | |
| 8.0 to 10 |
| Nickel (Ni), % | 19 to 22.5 | |
| 40.3 to 53.8 |
| Niobium (Nb), % | 0 to 0.3 | |
| 0 |
| Nitrogen (N), % | 0.1 to 0.3 | |
| 0 |
| Phosphorus (P), % | 0 to 0.040 | |
| 0 to 0.040 |
| Silicon (Si), % | 0.2 to 0.8 | |
| 0 to 1.0 |
| Sulfur (S), % | 0 to 0.015 | |
| 0 to 0.030 |
| Tantalum (Ta), % | 0.3 to 1.3 | |
| 0 |
| Tungsten (W), % | 2.0 to 3.5 | |
| 0.2 to 1.0 |
| Zinc (Zn), % | 0.0010 to 0.1 | |
| 0 |
| Residuals, % | 0 | |
| 0 to 0.5 |