R60704 Alloy vs. Z21210 Zinc

R60704 alloy belongs to the otherwise unclassified metals classification, while Z21210 zinc belongs to the zinc alloys. There are 8 material properties with values for both materials. Properties with values for just one material (17, in this case) are not shown.

For each property being compared, the top bar is R60704 alloy and the bottom bar is Z21210 zinc.

Metric UnitsUS Customary Units

Material Properties

Density, g/cm3 6.7
7.1
Specific Heat Capacity, J/kg-K 270
400
Strength to Weight: Axial, points 20
5.7 to 6.4
Strength to Weight: Bending, points 20
8.6 to 9.4
Tensile Strength: Ultimate (UTS), MPa 470
150 to 170
Thermal Conductivity, W/m-K 22
110
Thermal Diffusivity, mm2/s 12
38
Thermal Expansion, µm/m-K 6.0
32