R60705 Alloy vs. AISI 414 Stainless Steel

R60705 alloy belongs to the otherwise unclassified metals classification, while AISI 414 stainless steel belongs to the iron alloys. There are 21 material properties with values for both materials. Properties with values for just one material (12, in this case) are not shown.

For each property being compared, the top bar is R60705 alloy and the bottom bar is AISI 414 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 98
190
Elongation at Break, % 18
17
Fatigue Strength, MPa 290
430 to 480
Poisson's Ratio 0.34
0.28
Shear Modulus, GPa 37
76
Tensile Strength: Ultimate (UTS), MPa 540
900 to 960
Tensile Strength: Yield (Proof), MPa 430
700 to 790

Thermal Properties

Latent Heat of Fusion, J/g 250
280
Specific Heat Capacity, J/kg-K 270
480
Thermal Conductivity, W/m-K 17
25
Thermal Expansion, µm/m-K 6.3
10

Otherwise Unclassified Properties

Density, g/cm3 6.7
7.8
Embodied Water, L/kg 450
100

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 90
140 to 150
Resilience: Unit (Modulus of Resilience), kJ/m3 950
1260 to 1590
Stiffness to Weight: Axial, points 8.1
14
Stiffness to Weight: Bending, points 23
25
Strength to Weight: Axial, points 22
32 to 34
Strength to Weight: Bending, points 22
27 to 28
Thermal Diffusivity, mm2/s 9.5
6.7
Thermal Shock Resistance, points 63
33 to 35

Alloy Composition

Carbon (C), % 0 to 0.050
0 to 0.15
Chromium (Cr), % 0 to 0.2
11.5 to 13.5
Hafnium (Hf), % 0 to 4.5
0
Hydrogen (H), % 0 to 0.0050
0
Iron (Fe), % 0 to 0.2
81.8 to 87.3
Manganese (Mn), % 0
0 to 1.0
Nickel (Ni), % 0
1.3 to 2.5
Niobium (Nb), % 2.0 to 3.0
0
Nitrogen (N), % 0 to 0.025
0
Oxygen (O), % 0 to 0.18
0
Phosphorus (P), % 0
0 to 0.040
Silicon (Si), % 0
0 to 1.0
Sulfur (S), % 0
0 to 0.030
Zirconium (Zr), % 91 to 98
0