R60705 Alloy vs. EN 1.4935 Stainless Steel

R60705 alloy belongs to the otherwise unclassified metals classification, while EN 1.4935 stainless steel belongs to the iron alloys. There are 21 material properties with values for both materials. Properties with values for just one material (11, in this case) are not shown.

For each property being compared, the top bar is R60705 alloy and the bottom bar is EN 1.4935 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 98
200
Elongation at Break, % 18
16 to 18
Fatigue Strength, MPa 290
350 to 400
Poisson's Ratio 0.34
0.28
Shear Modulus, GPa 37
76
Tensile Strength: Ultimate (UTS), MPa 540
780 to 880
Tensile Strength: Yield (Proof), MPa 430
570 to 670

Thermal Properties

Latent Heat of Fusion, J/g 250
270
Specific Heat Capacity, J/kg-K 270
470
Thermal Conductivity, W/m-K 17
24
Thermal Expansion, µm/m-K 6.3
11

Otherwise Unclassified Properties

Density, g/cm3 6.7
7.8
Embodied Water, L/kg 450
100

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 90
130
Resilience: Unit (Modulus of Resilience), kJ/m3 950
830 to 1160
Stiffness to Weight: Axial, points 8.1
14
Stiffness to Weight: Bending, points 23
25
Strength to Weight: Axial, points 22
28 to 31
Strength to Weight: Bending, points 22
24 to 26
Thermal Diffusivity, mm2/s 9.5
6.5
Thermal Shock Resistance, points 63
27 to 30

Alloy Composition

Carbon (C), % 0 to 0.050
0.17 to 0.24
Chromium (Cr), % 0 to 0.2
11 to 12.5
Hafnium (Hf), % 0 to 4.5
0
Hydrogen (H), % 0 to 0.0050
0
Iron (Fe), % 0 to 0.2
83 to 86.7
Manganese (Mn), % 0
0.3 to 0.8
Molybdenum (Mo), % 0
0.8 to 1.2
Nickel (Ni), % 0
0.3 to 0.8
Niobium (Nb), % 2.0 to 3.0
0
Nitrogen (N), % 0 to 0.025
0
Oxygen (O), % 0 to 0.18
0
Phosphorus (P), % 0
0 to 0.025
Silicon (Si), % 0
0.1 to 0.5
Sulfur (S), % 0
0 to 0.015
Tungsten (W), % 0
0.4 to 0.6
Vanadium (V), % 0
0.2 to 0.35
Zirconium (Zr), % 91 to 98
0