R60706 Alloy vs. SAE-AISI 1005 Steel

R60706 alloy belongs to the otherwise unclassified metals classification, while SAE-AISI 1005 steel belongs to the iron alloys. There are 20 material properties with values for both materials. Properties with values for just one material (11, in this case) are not shown.

For each property being compared, the top bar is R60706 alloy and the bottom bar is SAE-AISI 1005 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 98
190
Elongation at Break, % 16
23
Poisson's Ratio 0.34
0.29
Shear Modulus, GPa 37
73
Tensile Strength: Ultimate (UTS), MPa 580
330
Tensile Strength: Yield (Proof), MPa 390
260

Thermal Properties

Latent Heat of Fusion, J/g 250
250
Specific Heat Capacity, J/kg-K 270
470
Thermal Conductivity, W/m-K 17
53
Thermal Expansion, µm/m-K 6.3
12

Otherwise Unclassified Properties

Density, g/cm3 6.7
7.9
Embodied Water, L/kg 450
45

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 82
70
Resilience: Unit (Modulus of Resilience), kJ/m3 760
180
Stiffness to Weight: Axial, points 8.1
13
Stiffness to Weight: Bending, points 23
24
Strength to Weight: Axial, points 24
12
Strength to Weight: Bending, points 23
13
Thermal Diffusivity, mm2/s 9.5
14
Thermal Shock Resistance, points 67
10

Alloy Composition

Carbon (C), % 0 to 0.050
0 to 0.060
Chromium (Cr), % 0 to 0.2
0
Hafnium (Hf), % 0 to 4.5
0
Hydrogen (H), % 0 to 0.0050
0
Iron (Fe), % 0 to 0.2
99.5 to 100
Manganese (Mn), % 0
0 to 0.35
Niobium (Nb), % 2.0 to 3.0
0
Nitrogen (N), % 0 to 0.025
0
Oxygen (O), % 0 to 0.16
0
Phosphorus (P), % 0
0 to 0.040
Sulfur (S), % 0
0 to 0.050
Zirconium (Zr), % 91 to 98
0