R60901 Alloy vs. Monel 400

R60901 alloy belongs to the otherwise unclassified metals classification, while Monel 400 belongs to the nickel alloys. There are 20 material properties with values for both materials. Properties with values for just one material (12, in this case) are not shown.

For each property being compared, the top bar is R60901 alloy and the bottom bar is Monel 400.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 98
160
Elongation at Break, % 17 to 22
20 to 40
Poisson's Ratio 0.34
0.32
Shear Modulus, GPa 37
62
Tensile Strength: Ultimate (UTS), MPa 500 to 580
540 to 780
Tensile Strength: Yield (Proof), MPa 350 to 390
210 to 590

Thermal Properties

Latent Heat of Fusion, J/g 250
270
Specific Heat Capacity, J/kg-K 270
430
Thermal Conductivity, W/m-K 17
23
Thermal Expansion, µm/m-K 6.3
14

Otherwise Unclassified Properties

Density, g/cm3 6.6
8.9
Embodied Water, L/kg 270
250

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 88 to 100
140 to 180
Resilience: Unit (Modulus of Resilience), kJ/m3 640 to 760
140 to 1080
Stiffness to Weight: Axial, points 8.3
10
Stiffness to Weight: Bending, points 23
21
Strength to Weight: Axial, points 21 to 25
17 to 25
Strength to Weight: Bending, points 21 to 24
17 to 21
Thermal Diffusivity, mm2/s 9.7
6.1
Thermal Shock Resistance, points 58 to 67
17 to 25

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
Carbon (C), % 0
0 to 0.3
Copper (Cu), % 0
28 to 34
Iron (Fe), % 0
0 to 2.5
Manganese (Mn), % 0
0 to 2.0
Nickel (Ni), % 0
63 to 72
Niobium (Nb), % 2.4 to 2.8
0
Silicon (Si), % 0
0 to 0.5
Sulfur (S), % 0
0 to 0.024
Zirconium (Zr), % 96.8 to 97.5
0
Residuals, % 0 to 0.29
0

Comparable Variants