S13800 Stainless Steel vs. AWS BAg-8

S13800 stainless steel belongs to the iron alloys classification, while AWS BAg-8 belongs to the otherwise unclassified metals. There are 15 material properties with values for both materials. Properties with values for just one material (21, in this case) are not shown.

For each property being compared, the top bar is S13800 stainless steel and the bottom bar is AWS BAg-8.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
84
Poisson's Ratio 0.28
0.36
Shear Modulus, GPa 77
31
Tensile Strength: Ultimate (UTS), MPa 980 to 1730
150

Thermal Properties

Latent Heat of Fusion, J/g 280
140
Melting Completion (Liquidus), °C 1450
780
Melting Onset (Solidus), °C 1410
780
Specific Heat Capacity, J/kg-K 470
280
Thermal Expansion, µm/m-K 11
19

Otherwise Unclassified Properties

Density, g/cm3 7.9
10

Common Calculations

Stiffness to Weight: Axial, points 14
4.6
Stiffness to Weight: Bending, points 25
14
Strength to Weight: Axial, points 35 to 61
4.1
Strength to Weight: Bending, points 28 to 41
6.2
Thermal Shock Resistance, points 33 to 58
6.7

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 460
Aluminum (Al), % 0.9 to 1.4
0
Carbon (C), % 0 to 0.050
0
Chromium (Cr), % 12.3 to 13.2
0
Copper (Cu), % 0
26.9 to 29
Iron (Fe), % 73.6 to 77.3
0
Manganese (Mn), % 0 to 0.2
0
Molybdenum (Mo), % 2.0 to 3.0
0
Nickel (Ni), % 7.5 to 8.5
0
Nitrogen (N), % 0 to 0.010
0
Phosphorus (P), % 0 to 0.010
0
Silicon (Si), % 0 to 0.1
0
Silver (Ag), % 0
71 to 73
Sulfur (S), % 0 to 0.0080
0
Residuals, % 0
0 to 0.15