S15500 Stainless Steel vs. ACI-ASTM CF3 Steel
Both S15500 stainless steel and ACI-ASTM CF3 steel are iron alloys. They have 89% of their average alloy composition in common. There are 32 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown.
For each property being compared, the top bar is S15500 stainless steel and the bottom bar is ACI-ASTM CF3 steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Brinell Hardness | 290 to 430 | |
| 140 |
| Elastic (Young's, Tensile) Modulus, GPa | 190 | |
| 200 |
| Elongation at Break, % | 6.8 to 16 | |
| 60 |
| Fatigue Strength, MPa | 350 to 650 | |
| 270 |
| Poisson's Ratio | 0.28 | |
| 0.28 |
| Shear Modulus, GPa | 75 | |
| 77 |
| Tensile Strength: Ultimate (UTS), MPa | 890 to 1490 | |
| 510 |
| Tensile Strength: Yield (Proof), MPa | 590 to 1310 | |
| 250 |
Thermal Properties
| Latent Heat of Fusion, J/g | 280 | |
| 300 |
| Maximum Temperature: Corrosion, °C | 440 | |
| 420 |
| Maximum Temperature: Mechanical, °C | 820 | |
| 960 |
| Melting Completion (Liquidus), °C | 1430 | |
| 1420 |
| Melting Onset (Solidus), °C | 1380 | |
| 1450 |
| Specific Heat Capacity, J/kg-K | 480 | |
| 480 |
| Thermal Conductivity, W/m-K | 17 | |
| 16 |
| Thermal Expansion, µm/m-K | 11 | |
| 16 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 2.2 | |
| 2.0 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 2.5 | |
| 2.3 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 13 | |
| 16 |
| Density, g/cm3 | 7.8 | |
| 7.8 |
| Embodied Carbon, kg CO2/kg material | 2.7 | |
| 3.2 |
| Embodied Energy, MJ/kg | 39 | |
| 45 |
| Embodied Water, L/kg | 130 | |
| 150 |
Common Calculations
| PREN (Pitting Resistance) | 15 | |
| 20 |
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 98 to 120 | |
| 250 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 890 to 4460 | |
| 160 |
| Stiffness to Weight: Axial, points | 14 | |
| 14 |
| Stiffness to Weight: Bending, points | 25 | |
| 25 |
| Strength to Weight: Axial, points | 32 to 53 | |
| 18 |
| Strength to Weight: Bending, points | 26 to 37 | |
| 18 |
| Thermal Diffusivity, mm2/s | 4.6 | |
| 4.3 |
| Thermal Shock Resistance, points | 30 to 50 | |
| 11 |
Alloy Composition
| Carbon (C), % | 0 to 0.070 | |
| 0 to 0.030 |
| Chromium (Cr), % | 14 to 15.5 | |
| 17 to 21 |
| Copper (Cu), % | 2.5 to 4.5 | |
| 0 |
| Iron (Fe), % | 71.9 to 79.9 | |
| 62.9 to 75 |
| Manganese (Mn), % | 0 to 1.0 | |
| 0 to 1.5 |
| Molybdenum (Mo), % | 0 | |
| 0 to 0.5 |
| Nickel (Ni), % | 3.5 to 5.5 | |
| 8.0 to 12 |
| Niobium (Nb), % | 0.15 to 0.45 | |
| 0 |
| Phosphorus (P), % | 0 to 0.040 | |
| 0 to 0.040 |
| Silicon (Si), % | 0 to 1.0 | |
| 0 to 2.0 |
| Sulfur (S), % | 0 to 0.030 | |
| 0 to 0.040 |