S15700 Stainless Steel vs. C64800 Bronze
S15700 stainless steel belongs to the iron alloys classification, while C64800 bronze belongs to the copper alloys. There are 29 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown.
For each property being compared, the top bar is S15700 stainless steel and the bottom bar is C64800 bronze.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 200 | |
| 120 |
| Elongation at Break, % | 1.1 to 29 | |
| 8.0 |
| Poisson's Ratio | 0.28 | |
| 0.34 |
| Shear Modulus, GPa | 77 | |
| 44 |
| Shear Strength, MPa | 770 to 1070 | |
| 380 |
| Tensile Strength: Ultimate (UTS), MPa | 1180 to 1890 | |
| 640 |
| Tensile Strength: Yield (Proof), MPa | 500 to 1770 | |
| 630 |
Thermal Properties
| Latent Heat of Fusion, J/g | 290 | |
| 220 |
| Maximum Temperature: Mechanical, °C | 870 | |
| 200 |
| Melting Completion (Liquidus), °C | 1440 | |
| 1090 |
| Melting Onset (Solidus), °C | 1400 | |
| 1030 |
| Specific Heat Capacity, J/kg-K | 480 | |
| 390 |
| Thermal Conductivity, W/m-K | 16 | |
| 260 |
| Thermal Expansion, µm/m-K | 11 | |
| 17 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 2.3 | |
| 65 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 2.6 | |
| 66 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 15 | |
| 33 |
| Density, g/cm3 | 7.8 | |
| 8.9 |
| Embodied Carbon, kg CO2/kg material | 3.4 | |
| 2.7 |
| Embodied Energy, MJ/kg | 47 | |
| 43 |
| Embodied Water, L/kg | 140 | |
| 310 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 17 to 270 | |
| 51 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 640 to 4660 | |
| 1680 |
| Stiffness to Weight: Axial, points | 14 | |
| 7.4 |
| Stiffness to Weight: Bending, points | 25 | |
| 18 |
| Strength to Weight: Axial, points | 42 to 67 | |
| 20 |
| Strength to Weight: Bending, points | 32 to 43 | |
| 19 |
| Thermal Diffusivity, mm2/s | 4.2 | |
| 75 |
| Thermal Shock Resistance, points | 39 to 63 | |
| 23 |
Alloy Composition
Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 460
| Aluminum (Al), % | 0.75 to 1.5 | |
| 0 |
| Carbon (C), % | 0 to 0.090 | |
| 0 |
| Chromium (Cr), % | 14 to 16 | |
| 0 to 0.090 |
| Cobalt (Co), % | 0 | |
| 1.0 to 3.0 |
| Copper (Cu), % | 0 | |
| 92.4 to 98.8 |
| Iron (Fe), % | 69.6 to 76.8 | |
| 0 to 1.0 |
| Lead (Pb), % | 0 | |
| 0 to 0.050 |
| Manganese (Mn), % | 0 to 1.0 | |
| 0 |
| Molybdenum (Mo), % | 2.0 to 3.0 | |
| 0 |
| Nickel (Ni), % | 6.5 to 7.7 | |
| 0 to 0.5 |
| Phosphorus (P), % | 0 to 0.040 | |
| 0 to 0.5 |
| Silicon (Si), % | 0 to 1.0 | |
| 0.2 to 1.0 |
| Sulfur (S), % | 0 to 0.030 | |
| 0 |
| Tin (Sn), % | 0 | |
| 0 to 0.5 |
| Zinc (Zn), % | 0 | |
| 0 to 0.5 |
| Residuals, % | 0 | |
| 0 to 0.5 |