S17400 Stainless Steel vs. 2007 Aluminum
S17400 stainless steel belongs to the iron alloys classification, while 2007 aluminum belongs to the aluminum alloys. There are 30 material properties with values for both materials. Properties with values for just one material (6, in this case) are not shown. Please note that the two materials have significantly dissimilar densities. This means that additional care is required when interpreting the data, because some material properties are based on units of mass, while others are based on units of area or volume.
For each property being compared, the top bar is S17400 stainless steel and the bottom bar is 2007 aluminum.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 190 | |
| 71 |
| Elongation at Break, % | 11 to 21 | |
| 5.6 to 8.0 |
| Fatigue Strength, MPa | 380 to 670 | |
| 91 to 110 |
| Poisson's Ratio | 0.28 | |
| 0.33 |
| Shear Modulus, GPa | 75 | |
| 27 |
| Shear Strength, MPa | 570 to 830 | |
| 220 to 250 |
| Tensile Strength: Ultimate (UTS), MPa | 910 to 1390 | |
| 370 to 420 |
| Tensile Strength: Yield (Proof), MPa | 580 to 1250 | |
| 240 to 270 |
Thermal Properties
| Latent Heat of Fusion, J/g | 280 | |
| 390 |
| Maximum Temperature: Mechanical, °C | 850 | |
| 190 |
| Melting Completion (Liquidus), °C | 1440 | |
| 640 |
| Melting Onset (Solidus), °C | 1400 | |
| 510 |
| Specific Heat Capacity, J/kg-K | 480 | |
| 870 |
| Thermal Conductivity, W/m-K | 17 | |
| 130 |
| Thermal Expansion, µm/m-K | 11 | |
| 23 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 2.3 | |
| 47 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 2.6 | |
| 140 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 14 | |
| 11 |
| Density, g/cm3 | 7.8 | |
| 3.1 |
| Embodied Carbon, kg CO2/kg material | 2.7 | |
| 8.0 |
| Embodied Energy, MJ/kg | 39 | |
| 150 |
| Embodied Water, L/kg | 130 | |
| 1130 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 140 to 160 | |
| 21 to 26 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 880 to 4060 | |
| 390 to 530 |
| Stiffness to Weight: Axial, points | 14 | |
| 13 |
| Stiffness to Weight: Bending, points | 25 | |
| 44 |
| Strength to Weight: Axial, points | 32 to 49 | |
| 33 to 38 |
| Strength to Weight: Bending, points | 27 to 35 | |
| 37 to 40 |
| Thermal Diffusivity, mm2/s | 4.5 | |
| 48 |
| Thermal Shock Resistance, points | 30 to 46 | |
| 16 to 19 |
Alloy Composition
Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 460
| Aluminum (Al), % | 0 | |
| 87.5 to 95 |
| Bismuth (Bi), % | 0 | |
| 0 to 0.2 |
| Carbon (C), % | 0 to 0.070 | |
| 0 |
| Chromium (Cr), % | 15 to 17 | |
| 0 to 0.1 |
| Copper (Cu), % | 3.0 to 5.0 | |
| 3.3 to 4.6 |
| Iron (Fe), % | 70.4 to 78.9 | |
| 0 to 0.8 |
| Lead (Pb), % | 0 | |
| 0.8 to 1.5 |
| Magnesium (Mg), % | 0 | |
| 0.4 to 1.8 |
| Manganese (Mn), % | 0 to 1.0 | |
| 0.5 to 1.0 |
| Nickel (Ni), % | 3.0 to 5.0 | |
| 0 to 0.2 |
| Niobium (Nb), % | 0.15 to 0.45 | |
| 0 |
| Phosphorus (P), % | 0 to 0.040 | |
| 0 |
| Silicon (Si), % | 0 to 1.0 | |
| 0 to 0.8 |
| Sulfur (S), % | 0 to 0.030 | |
| 0 |
| Tin (Sn), % | 0 | |
| 0 to 0.2 |
| Titanium (Ti), % | 0 | |
| 0 to 0.2 |
| Zinc (Zn), % | 0 | |
| 0 to 0.8 |
| Residuals, % | 0 | |
| 0 to 0.3 |