S17700 Stainless Steel vs. SAE-AISI 1030 Steel
Both S17700 stainless steel and SAE-AISI 1030 steel are iron alloys. They have 74% of their average alloy composition in common. There are 31 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown.
For each property being compared, the top bar is S17700 stainless steel and the bottom bar is SAE-AISI 1030 steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Brinell Hardness | 180 to 430 | |
| 150 to 160 |
| Elastic (Young's, Tensile) Modulus, GPa | 200 | |
| 190 |
| Elongation at Break, % | 1.0 to 23 | |
| 14 to 22 |
| Fatigue Strength, MPa | 290 to 560 | |
| 210 to 320 |
| Poisson's Ratio | 0.28 | |
| 0.29 |
| Shear Modulus, GPa | 76 | |
| 73 |
| Shear Strength, MPa | 740 to 940 | |
| 330 to 360 |
| Tensile Strength: Ultimate (UTS), MPa | 1180 to 1650 | |
| 530 to 590 |
| Tensile Strength: Yield (Proof), MPa | 430 to 1210 | |
| 300 to 490 |
Thermal Properties
| Latent Heat of Fusion, J/g | 290 | |
| 250 |
| Maximum Temperature: Mechanical, °C | 890 | |
| 400 |
| Melting Completion (Liquidus), °C | 1440 | |
| 1460 |
| Melting Onset (Solidus), °C | 1400 | |
| 1420 |
| Specific Heat Capacity, J/kg-K | 480 | |
| 470 |
| Thermal Conductivity, W/m-K | 15 | |
| 51 |
| Thermal Expansion, µm/m-K | 11 | |
| 12 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 2.3 | |
| 7.0 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 2.7 | |
| 8.0 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 13 | |
| 1.8 |
| Density, g/cm3 | 7.7 | |
| 7.8 |
| Embodied Carbon, kg CO2/kg material | 2.8 | |
| 1.4 |
| Embodied Energy, MJ/kg | 40 | |
| 18 |
| Embodied Water, L/kg | 150 | |
| 46 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 15 to 210 | |
| 77 to 100 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 460 to 3750 | |
| 230 to 650 |
| Stiffness to Weight: Axial, points | 14 | |
| 13 |
| Stiffness to Weight: Bending, points | 25 | |
| 24 |
| Strength to Weight: Axial, points | 42 to 59 | |
| 19 to 21 |
| Strength to Weight: Bending, points | 32 to 40 | |
| 18 to 20 |
| Thermal Diffusivity, mm2/s | 4.1 | |
| 14 |
| Thermal Shock Resistance, points | 39 to 54 | |
| 17 to 19 |
Alloy Composition
| Aluminum (Al), % | 0.75 to 1.5 | |
| 0 |
| Carbon (C), % | 0 to 0.090 | |
| 0.28 to 0.34 |
| Chromium (Cr), % | 16 to 18 | |
| 0 |
| Iron (Fe), % | 70.5 to 76.8 | |
| 98.7 to 99.12 |
| Manganese (Mn), % | 0 to 1.0 | |
| 0.6 to 0.9 |
| Nickel (Ni), % | 6.5 to 7.8 | |
| 0 |
| Phosphorus (P), % | 0 to 0.040 | |
| 0 to 0.040 |
| Silicon (Si), % | 0 to 1.0 | |
| 0 |
| Sulfur (S), % | 0 to 0.030 | |
| 0 to 0.050 |