S20432 Stainless Steel vs. EN 1.0314 Steel

Both S20432 stainless steel and EN 1.0314 steel are iron alloys. They have 71% of their average alloy composition in common. There are 31 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown.

For each property being compared, the top bar is S20432 stainless steel and the bottom bar is EN 1.0314 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 170
92 to 120
Elastic (Young's, Tensile) Modulus, GPa 200
190
Elongation at Break, % 45
24 to 25
Fatigue Strength, MPa 210
140 to 220
Poisson's Ratio 0.28
0.29
Shear Modulus, GPa 76
73
Shear Strength, MPa 400
200 to 250
Tensile Strength: Ultimate (UTS), MPa 580
320 to 400
Tensile Strength: Yield (Proof), MPa 230
190 to 310

Thermal Properties

Latent Heat of Fusion, J/g 280
250
Maximum Temperature: Mechanical, °C 900
400
Melting Completion (Liquidus), °C 1410
1470
Melting Onset (Solidus), °C 1370
1430
Specific Heat Capacity, J/kg-K 480
470
Thermal Conductivity, W/m-K 15
53
Thermal Expansion, µm/m-K 17
12

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.4
6.9
Electrical Conductivity: Equal Weight (Specific), % IACS 2.8
7.9

Otherwise Unclassified Properties

Base Metal Price, % relative 13
1.8
Density, g/cm3 7.8
7.9
Embodied Carbon, kg CO2/kg material 2.7
1.4
Embodied Energy, MJ/kg 38
18
Embodied Water, L/kg 140
46

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 210
68 to 87
Resilience: Unit (Modulus of Resilience), kJ/m3 140
95 to 250
Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 25
24
Strength to Weight: Axial, points 21
11 to 14
Strength to Weight: Bending, points 20
13 to 15
Thermal Diffusivity, mm2/s 4.0
14
Thermal Shock Resistance, points 13
10 to 13

Alloy Composition

Aluminum (Al), % 0
0.020 to 0.060
Carbon (C), % 0 to 0.080
0 to 0.030
Chromium (Cr), % 17 to 18
0
Copper (Cu), % 2.0 to 3.0
0
Iron (Fe), % 66.7 to 74
99.365 to 99.78
Manganese (Mn), % 3.0 to 5.0
0.2 to 0.4
Nickel (Ni), % 4.0 to 6.0
0
Nitrogen (N), % 0.050 to 0.2
0
Phosphorus (P), % 0 to 0.045
0 to 0.020
Silicon (Si), % 0 to 1.0
0 to 0.1
Sulfur (S), % 0 to 0.030
0 to 0.025