S20432 Stainless Steel vs. EN 1.1131 Cast Steel

Both S20432 stainless steel and EN 1.1131 cast steel are iron alloys. They have 72% of their average alloy composition in common. There are 29 material properties with values for both materials. Properties with values for just one material (6, in this case) are not shown.

For each property being compared, the top bar is S20432 stainless steel and the bottom bar is EN 1.1131 cast steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
190
Elongation at Break, % 45
27
Fatigue Strength, MPa 210
200
Poisson's Ratio 0.28
0.29
Shear Modulus, GPa 76
73
Tensile Strength: Ultimate (UTS), MPa 580
530
Tensile Strength: Yield (Proof), MPa 230
270

Thermal Properties

Latent Heat of Fusion, J/g 280
250
Maximum Temperature: Mechanical, °C 900
400
Melting Completion (Liquidus), °C 1410
1460
Melting Onset (Solidus), °C 1370
1420
Specific Heat Capacity, J/kg-K 480
470
Thermal Conductivity, W/m-K 15
52
Thermal Expansion, µm/m-K 17
12

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.4
7.1
Electrical Conductivity: Equal Weight (Specific), % IACS 2.8
8.2

Otherwise Unclassified Properties

Base Metal Price, % relative 13
1.9
Density, g/cm3 7.8
7.8
Embodied Carbon, kg CO2/kg material 2.7
1.4
Embodied Energy, MJ/kg 38
19
Embodied Water, L/kg 140
47

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 210
120
Resilience: Unit (Modulus of Resilience), kJ/m3 140
200
Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 25
24
Strength to Weight: Axial, points 21
19
Strength to Weight: Bending, points 20
18
Thermal Diffusivity, mm2/s 4.0
14
Thermal Shock Resistance, points 13
17

Alloy Composition

Carbon (C), % 0 to 0.080
0.15 to 0.2
Chromium (Cr), % 17 to 18
0
Copper (Cu), % 2.0 to 3.0
0
Iron (Fe), % 66.7 to 74
97.6 to 98.9
Manganese (Mn), % 3.0 to 5.0
1.0 to 1.6
Nickel (Ni), % 4.0 to 6.0
0
Nitrogen (N), % 0.050 to 0.2
0
Phosphorus (P), % 0 to 0.045
0 to 0.020
Silicon (Si), % 0 to 1.0
0 to 0.6
Sulfur (S), % 0 to 0.030
0 to 0.030