EN 1.1131 (G17Mn5) Cast Non-Alloy Steel

EN 1.1131 cast steel is a carbon steel formulated for casting. Cited properties are appropriate for the quenched and tempered condition. 1.1131 is the EN numeric designation for this material. G17Mn5 is the EN chemical designation.

It has a moderately high ductility among the cast carbon steels in the database.

The graph bars on the material properties cards below compare EN 1.1131 cast steel to: cast carbon steels (top), all iron alloys (middle), and the entire database (bottom). A full bar means this is the highest value in the relevant set. A half-full bar means it's 50% of the highest, and so on.

Mechanical Properties

Elastic (Young's, Tensile) Modulus

190 GPa 27 x 106 psi

Elongation at Break

27 %

Fatigue Strength

200 MPa 29 x 103 psi

Impact Strength: V-Notched Charpy

78 J 58 ft-lb

Poisson's Ratio

0.29

Shear Modulus

73 GPa 11 x 106 psi

Tensile Strength: Ultimate (UTS)

530 MPa 76 x 103 psi

Tensile Strength: Yield (Proof)

270 MPa 39 x 103 psi

Thermal Properties

Latent Heat of Fusion

250 J/g

Maximum Temperature: Mechanical

400 °C 750 °F

Melting Completion (Liquidus)

1460 °C 2660 °F

Melting Onset (Solidus)

1420 °C 2580 °F

Specific Heat Capacity

470 J/kg-K 0.11 BTU/lb-°F

Thermal Conductivity

52 W/m-K 30 BTU/h-ft-°F

Thermal Expansion

12 µm/m-K

Electrical Properties

Electrical Conductivity: Equal Volume

7.1 % IACS

Electrical Conductivity: Equal Weight (Specific)

8.2 % IACS

Otherwise Unclassified Properties

Base Metal Price

1.9 % relative

Density

7.8 g/cm3 490 lb/ft3

Embodied Carbon

1.4 kg CO2/kg material

Embodied Energy

19 MJ/kg 8.0 x 103 BTU/lb

Embodied Water

47 L/kg 5.6 gal/lb

Common Calculations

Resilience: Ultimate (Unit Rupture Work)

120 MJ/m3

Resilience: Unit (Modulus of Resilience)

200 kJ/m3

Stiffness to Weight: Axial

13 points

Stiffness to Weight: Bending

24 points

Strength to Weight: Axial

19 points

Strength to Weight: Bending

18 points

Thermal Diffusivity

14 mm2/s

Thermal Shock Resistance

17 points

Alloy Composition

Iron (Fe)Fe 97.6 to 98.9
Manganese (Mn)Mn 1.0 to 1.6
Silicon (Si)Si 0 to 0.6
Carbon (C)C 0.15 to 0.2
Sulfur (S)S 0 to 0.030
Phosphorus (P)P 0 to 0.020

All values are % weight. Ranges represent what is permitted under applicable standards.

Followup Questions

Similar Alloys

Further Reading

ISO 4991: Steel castings for pressure purposes

EN 10293: Steel castings - Steel castings for general engineering uses

Properties and Selection: Irons, Steels and High Performance Alloys, ASM Handbook vol. 1, ASM International, 1993

Carbon Steel Handbook, D. Gandy, 2007

Ferrous Materials: Steel and Cast Iron, Hans Berns and Werner Theisen, 2008

Steels: Processing, Structure, and Performance, 2nd ed., George Krauss, 2015