S20432 Stainless Steel vs. EN 1.1132 Steel

Both S20432 stainless steel and EN 1.1132 steel are iron alloys. They have 71% of their average alloy composition in common. There are 31 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown.

For each property being compared, the top bar is S20432 stainless steel and the bottom bar is EN 1.1132 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 170
110 to 140
Elastic (Young's, Tensile) Modulus, GPa 200
190
Elongation at Break, % 45
12 to 24
Fatigue Strength, MPa 210
180 to 280
Poisson's Ratio 0.28
0.29
Shear Modulus, GPa 76
73
Shear Strength, MPa 400
260 to 310
Tensile Strength: Ultimate (UTS), MPa 580
370 to 490
Tensile Strength: Yield (Proof), MPa 230
240 to 400

Thermal Properties

Latent Heat of Fusion, J/g 280
250
Maximum Temperature: Mechanical, °C 900
400
Melting Completion (Liquidus), °C 1410
1460
Melting Onset (Solidus), °C 1370
1420
Specific Heat Capacity, J/kg-K 480
470
Thermal Conductivity, W/m-K 15
51
Thermal Expansion, µm/m-K 17
12

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.4
7.0
Electrical Conductivity: Equal Weight (Specific), % IACS 2.8
8.0

Otherwise Unclassified Properties

Base Metal Price, % relative 13
1.8
Density, g/cm3 7.8
7.9
Embodied Carbon, kg CO2/kg material 2.7
1.4
Embodied Energy, MJ/kg 38
18
Embodied Water, L/kg 140
46

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 210
38 to 110
Resilience: Unit (Modulus of Resilience), kJ/m3 140
160 to 430
Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 25
24
Strength to Weight: Axial, points 21
13 to 17
Strength to Weight: Bending, points 20
15 to 18
Thermal Diffusivity, mm2/s 4.0
14
Thermal Shock Resistance, points 13
12 to 16

Alloy Composition

Carbon (C), % 0 to 0.080
0.13 to 0.17
Chromium (Cr), % 17 to 18
0
Copper (Cu), % 2.0 to 3.0
0 to 0.25
Iron (Fe), % 66.7 to 74
98.6 to 99.57
Manganese (Mn), % 3.0 to 5.0
0.3 to 0.6
Nickel (Ni), % 4.0 to 6.0
0
Nitrogen (N), % 0.050 to 0.2
0
Phosphorus (P), % 0 to 0.045
0 to 0.025
Silicon (Si), % 0 to 1.0
0 to 0.3
Sulfur (S), % 0 to 0.030
0 to 0.025