S24000 Stainless Steel vs. EN 1.4806 Stainless Steel

Both S24000 stainless steel and EN 1.4806 stainless steel are iron alloys. They have 66% of their average alloy composition in common. There are 28 material properties with values for both materials. Properties with values for just one material (7, in this case) are not shown.

For each property being compared, the top bar is S24000 stainless steel and the bottom bar is EN 1.4806 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 210
140
Elastic (Young's, Tensile) Modulus, GPa 200
190
Elongation at Break, % 39
6.8
Fatigue Strength, MPa 370
120
Poisson's Ratio 0.28
0.28
Shear Modulus, GPa 77
75
Tensile Strength: Ultimate (UTS), MPa 770
470
Tensile Strength: Yield (Proof), MPa 430
250

Thermal Properties

Latent Heat of Fusion, J/g 280
320
Maximum Temperature: Corrosion, °C 410
400
Maximum Temperature: Mechanical, °C 910
1000
Melting Completion (Liquidus), °C 1390
1380
Melting Onset (Solidus), °C 1350
1340
Specific Heat Capacity, J/kg-K 480
480
Thermal Expansion, µm/m-K 17
15

Otherwise Unclassified Properties

Base Metal Price, % relative 12
31
Density, g/cm3 7.6
8.0
Embodied Carbon, kg CO2/kg material 2.7
5.4
Embodied Energy, MJ/kg 39
76
Embodied Water, L/kg 150
190

Common Calculations

PREN (Pitting Resistance) 23
18
Resilience: Ultimate (Unit Rupture Work), MJ/m3 260
27
Resilience: Unit (Modulus of Resilience), kJ/m3 470
160
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 25
24
Strength to Weight: Axial, points 28
16
Strength to Weight: Bending, points 24
17
Thermal Shock Resistance, points 16
11

Alloy Composition

Carbon (C), % 0 to 0.080
0.3 to 0.5
Chromium (Cr), % 17 to 19
16 to 18
Iron (Fe), % 61.5 to 69
40.4 to 48.7
Manganese (Mn), % 11.5 to 14.5
0 to 2.0
Molybdenum (Mo), % 0
0 to 0.5
Nickel (Ni), % 2.3 to 3.7
34 to 36
Nitrogen (N), % 0.2 to 0.4
0
Phosphorus (P), % 0 to 0.060
0 to 0.040
Silicon (Si), % 0 to 0.75
1.0 to 2.5
Sulfur (S), % 0 to 0.030
0 to 0.030