S24000 Stainless Steel vs. EN 1.5503 Steel
Both S24000 stainless steel and EN 1.5503 steel are iron alloys. They have 66% of their average alloy composition in common. There are 28 material properties with values for both materials. Properties with values for just one material (7, in this case) are not shown.
For each property being compared, the top bar is S24000 stainless steel and the bottom bar is EN 1.5503 steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Brinell Hardness | 210 | |
| 120 to 160 |
| Elastic (Young's, Tensile) Modulus, GPa | 200 | |
| 190 |
| Elongation at Break, % | 39 | |
| 12 to 17 |
| Fatigue Strength, MPa | 370 | |
| 180 to 280 |
| Poisson's Ratio | 0.28 | |
| 0.29 |
| Reduction in Area, % | 57 | |
| 63 to 72 |
| Shear Modulus, GPa | 77 | |
| 73 |
| Shear Strength, MPa | 530 | |
| 270 to 320 |
| Tensile Strength: Ultimate (UTS), MPa | 770 | |
| 400 to 520 |
| Tensile Strength: Yield (Proof), MPa | 430 | |
| 270 to 430 |
Thermal Properties
| Latent Heat of Fusion, J/g | 280 | |
| 250 |
| Maximum Temperature: Mechanical, °C | 910 | |
| 400 |
| Melting Completion (Liquidus), °C | 1390 | |
| 1460 |
| Melting Onset (Solidus), °C | 1350 | |
| 1420 |
| Specific Heat Capacity, J/kg-K | 480 | |
| 470 |
| Thermal Expansion, µm/m-K | 17 | |
| 13 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 12 | |
| 1.8 |
| Density, g/cm3 | 7.6 | |
| 7.8 |
| Embodied Carbon, kg CO2/kg material | 2.7 | |
| 1.4 |
| Embodied Energy, MJ/kg | 39 | |
| 18 |
| Embodied Water, L/kg | 150 | |
| 46 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 260 | |
| 41 to 81 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 470 | |
| 200 to 490 |
| Stiffness to Weight: Axial, points | 14 | |
| 13 |
| Stiffness to Weight: Bending, points | 25 | |
| 24 |
| Strength to Weight: Axial, points | 28 | |
| 14 to 19 |
| Strength to Weight: Bending, points | 24 | |
| 15 to 18 |
| Thermal Shock Resistance, points | 16 | |
| 12 to 15 |
Alloy Composition
| Boron (B), % | 0 | |
| 0.00080 to 0.0050 |
| Carbon (C), % | 0 to 0.080 | |
| 0.16 to 0.2 |
| Chromium (Cr), % | 17 to 19 | |
| 0 |
| Copper (Cu), % | 0 | |
| 0 to 0.25 |
| Iron (Fe), % | 61.5 to 69 | |
| 98.4 to 99.239 |
| Manganese (Mn), % | 11.5 to 14.5 | |
| 0.6 to 0.8 |
| Nickel (Ni), % | 2.3 to 3.7 | |
| 0 |
| Nitrogen (N), % | 0.2 to 0.4 | |
| 0 |
| Phosphorus (P), % | 0 to 0.060 | |
| 0 to 0.025 |
| Silicon (Si), % | 0 to 0.75 | |
| 0 to 0.3 |
| Sulfur (S), % | 0 to 0.030 | |
| 0 to 0.025 |