S31277 stainless steel belongs to the iron alloys classification, while 5449 aluminum belongs to the aluminum alloys. There are 26 material properties with values for both materials. Properties with values for just one material (6, in this case) are not shown. Please note that the two materials have significantly dissimilar densities. This means that additional care is required when interpreting the data, because some material properties are based on units of mass, while others are based on units of area or volume.

For each property being compared, the top bar is S31277 stainless steel and the bottom bar is 5449 aluminum.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 210
69
Elongation at Break, % 45
4.0 to 17
Fatigue Strength, MPa 380
78 to 120
Poisson's Ratio 0.28
0.33
Shear Modulus, GPa 80
26
Shear Strength, MPa 600
130 to 190
Tensile Strength: Ultimate (UTS), MPa 860
210 to 330
Tensile Strength: Yield (Proof), MPa 410
91 to 260

Thermal Properties

Latent Heat of Fusion, J/g 310
400
Maximum Temperature: Mechanical, °C 1100
190
Melting Completion (Liquidus), °C 1460
650
Melting Onset (Solidus), °C 1410
590
Specific Heat Capacity, J/kg-K 460
900
Thermal Expansion, µm/m-K 16
23

Otherwise Unclassified Properties

Base Metal Price, % relative 36
9.5
Density, g/cm3 8.1
2.8
Embodied Carbon, kg CO2/kg material 6.7
8.5
Embodied Energy, MJ/kg 90
150
Embodied Water, L/kg 220
1180

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 320
12 to 29
Resilience: Unit (Modulus of Resilience), kJ/m3 410
60 to 480
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 24
50
Strength to Weight: Axial, points 29
22 to 33
Strength to Weight: Bending, points 25
29 to 39
Thermal Shock Resistance, points 19
9.4 to 15

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 460
Aluminum (Al), % 0
94.1 to 97.8
Carbon (C), % 0 to 0.020
0
Chromium (Cr), % 20.5 to 23
0 to 0.3
Copper (Cu), % 0.5 to 1.5
0 to 0.3
Iron (Fe), % 35.5 to 46.2
0 to 0.7
Magnesium (Mg), % 0
1.6 to 2.6
Manganese (Mn), % 0 to 3.0
0.6 to 1.1
Molybdenum (Mo), % 6.5 to 8.0
0
Nickel (Ni), % 26 to 28
0
Nitrogen (N), % 0.3 to 0.4
0
Phosphorus (P), % 0 to 0.030
0
Silicon (Si), % 0 to 0.5
0 to 0.4
Sulfur (S), % 0 to 0.010
0
Titanium (Ti), % 0
0 to 0.1
Zinc (Zn), % 0
0 to 0.3
Residuals, % 0
0 to 0.15