S31277 Stainless Steel vs. EN 1.7239 Steel

Both S31277 stainless steel and EN 1.7239 steel are iron alloys. They have 43% of their average alloy composition in common. There are 20 material properties with values for both materials. Properties with values for just one material (13, in this case) are not shown.

For each property being compared, the top bar is S31277 stainless steel and the bottom bar is EN 1.7239 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 210
190
Poisson's Ratio 0.28
0.29
Shear Modulus, GPa 80
73
Tensile Strength: Ultimate (UTS), MPa 860
660 to 1990

Thermal Properties

Latent Heat of Fusion, J/g 310
250
Maximum Temperature: Mechanical, °C 1100
420
Melting Completion (Liquidus), °C 1460
1460
Melting Onset (Solidus), °C 1410
1410
Specific Heat Capacity, J/kg-K 460
470
Thermal Expansion, µm/m-K 16
13

Otherwise Unclassified Properties

Base Metal Price, % relative 36
2.3
Density, g/cm3 8.1
7.8
Embodied Carbon, kg CO2/kg material 6.7
1.5
Embodied Energy, MJ/kg 90
20
Embodied Water, L/kg 220
50

Common Calculations

Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 24
24
Strength to Weight: Axial, points 29
23 to 71
Strength to Weight: Bending, points 25
21 to 45
Thermal Shock Resistance, points 19
19 to 59

Alloy Composition

Carbon (C), % 0 to 0.020
0.56 to 0.64
Chromium (Cr), % 20.5 to 23
0.7 to 1.0
Copper (Cu), % 0.5 to 1.5
0
Iron (Fe), % 35.5 to 46.2
96.8 to 98
Manganese (Mn), % 0 to 3.0
0.7 to 1.0
Molybdenum (Mo), % 6.5 to 8.0
0.060 to 0.15
Nickel (Ni), % 26 to 28
0
Nitrogen (N), % 0.3 to 0.4
0
Phosphorus (P), % 0 to 0.030
0 to 0.025
Silicon (Si), % 0 to 0.5
0 to 0.4
Sulfur (S), % 0 to 0.010
0 to 0.025