S31277 Stainless Steel vs. SAE-AISI 8645 Steel
Both S31277 stainless steel and SAE-AISI 8645 steel are iron alloys. They have 43% of their average alloy composition in common. There are 26 material properties with values for both materials. Properties with values for just one material (7, in this case) are not shown.
For each property being compared, the top bar is S31277 stainless steel and the bottom bar is SAE-AISI 8645 steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 210 | |
| 190 |
| Elongation at Break, % | 45 | |
| 12 to 23 |
| Fatigue Strength, MPa | 380 | |
| 280 to 350 |
| Poisson's Ratio | 0.28 | |
| 0.29 |
| Shear Modulus, GPa | 80 | |
| 73 |
| Shear Strength, MPa | 600 | |
| 380 to 400 |
| Tensile Strength: Ultimate (UTS), MPa | 860 | |
| 600 to 670 |
| Tensile Strength: Yield (Proof), MPa | 410 | |
| 390 to 560 |
Thermal Properties
| Latent Heat of Fusion, J/g | 310 | |
| 250 |
| Maximum Temperature: Mechanical, °C | 1100 | |
| 410 |
| Melting Completion (Liquidus), °C | 1460 | |
| 1460 |
| Melting Onset (Solidus), °C | 1410 | |
| 1420 |
| Specific Heat Capacity, J/kg-K | 460 | |
| 470 |
| Thermal Expansion, µm/m-K | 16 | |
| 13 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 36 | |
| 2.6 |
| Density, g/cm3 | 8.1 | |
| 7.8 |
| Embodied Carbon, kg CO2/kg material | 6.7 | |
| 1.5 |
| Embodied Energy, MJ/kg | 90 | |
| 20 |
| Embodied Water, L/kg | 220 | |
| 50 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 320 | |
| 77 to 120 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 410 | |
| 420 to 840 |
| Stiffness to Weight: Axial, points | 14 | |
| 13 |
| Stiffness to Weight: Bending, points | 24 | |
| 24 |
| Strength to Weight: Axial, points | 29 | |
| 21 to 24 |
| Strength to Weight: Bending, points | 25 | |
| 20 to 22 |
| Thermal Shock Resistance, points | 19 | |
| 18 to 20 |
Alloy Composition
| Carbon (C), % | 0 to 0.020 | |
| 0.43 to 0.48 |
| Chromium (Cr), % | 20.5 to 23 | |
| 0.4 to 0.6 |
| Copper (Cu), % | 0.5 to 1.5 | |
| 0 |
| Iron (Fe), % | 35.5 to 46.2 | |
| 96.5 to 97.7 |
| Manganese (Mn), % | 0 to 3.0 | |
| 0.75 to 1.0 |
| Molybdenum (Mo), % | 6.5 to 8.0 | |
| 0.15 to 0.25 |
| Nickel (Ni), % | 26 to 28 | |
| 0.4 to 0.7 |
| Nitrogen (N), % | 0.3 to 0.4 | |
| 0 |
| Phosphorus (P), % | 0 to 0.030 | |
| 0 to 0.035 |
| Silicon (Si), % | 0 to 0.5 | |
| 0.15 to 0.35 |
| Sulfur (S), % | 0 to 0.010 | |
| 0 to 0.040 |