S31277 Stainless Steel vs. SAE-AISI 8660 Steel

Both S31277 stainless steel and SAE-AISI 8660 steel are iron alloys. They have 43% of their average alloy composition in common. There are 26 material properties with values for both materials. Properties with values for just one material (7, in this case) are not shown.

For each property being compared, the top bar is S31277 stainless steel and the bottom bar is SAE-AISI 8660 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 210
190
Elongation at Break, % 45
12
Fatigue Strength, MPa 380
340
Poisson's Ratio 0.28
0.29
Shear Modulus, GPa 80
73
Shear Strength, MPa 600
390
Tensile Strength: Ultimate (UTS), MPa 860
660
Tensile Strength: Yield (Proof), MPa 410
550

Thermal Properties

Latent Heat of Fusion, J/g 310
250
Maximum Temperature: Mechanical, °C 1100
410
Melting Completion (Liquidus), °C 1460
1450
Melting Onset (Solidus), °C 1410
1410
Specific Heat Capacity, J/kg-K 460
470
Thermal Expansion, µm/m-K 16
13

Otherwise Unclassified Properties

Base Metal Price, % relative 36
2.6
Density, g/cm3 8.1
7.8
Embodied Carbon, kg CO2/kg material 6.7
1.5
Embodied Energy, MJ/kg 90
20
Embodied Water, L/kg 220
50

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 320
73
Resilience: Unit (Modulus of Resilience), kJ/m3 410
800
Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 24
24
Strength to Weight: Axial, points 29
23
Strength to Weight: Bending, points 25
21
Thermal Shock Resistance, points 19
19

Alloy Composition

Carbon (C), % 0 to 0.020
0.56 to 0.64
Chromium (Cr), % 20.5 to 23
0.4 to 0.6
Copper (Cu), % 0.5 to 1.5
0
Iron (Fe), % 35.5 to 46.2
96.4 to 97.6
Manganese (Mn), % 0 to 3.0
0.75 to 1.0
Molybdenum (Mo), % 6.5 to 8.0
0.15 to 0.25
Nickel (Ni), % 26 to 28
0.4 to 0.7
Nitrogen (N), % 0.3 to 0.4
0
Phosphorus (P), % 0 to 0.030
0 to 0.035
Silicon (Si), % 0 to 0.5
0.15 to 0.35
Sulfur (S), % 0 to 0.010
0 to 0.040