S32053 Stainless Steel vs. AISI 409 Stainless Steel

Both S32053 stainless steel and AISI 409 stainless steel are iron alloys. Both are furnished in the annealed condition. They have 58% of their average alloy composition in common. There are 32 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown.

For each property being compared, the top bar is S32053 stainless steel and the bottom bar is AISI 409 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 210
190
Elongation at Break, % 46
24
Fatigue Strength, MPa 310
140
Poisson's Ratio 0.28
0.28
Shear Modulus, GPa 80
75
Shear Strength, MPa 510
270
Tensile Strength: Ultimate (UTS), MPa 730
420
Tensile Strength: Yield (Proof), MPa 330
200

Thermal Properties

Latent Heat of Fusion, J/g 310
270
Maximum Temperature: Corrosion, °C 440
450
Maximum Temperature: Mechanical, °C 1100
710
Melting Completion (Liquidus), °C 1450
1450
Melting Onset (Solidus), °C 1400
1400
Specific Heat Capacity, J/kg-K 470
480
Thermal Conductivity, W/m-K 13
25
Thermal Expansion, µm/m-K 16
11

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 1.8
2.9
Electrical Conductivity: Equal Weight (Specific), % IACS 2.0
3.3

Otherwise Unclassified Properties

Base Metal Price, % relative 33
6.5
Density, g/cm3 8.1
7.7
Embodied Carbon, kg CO2/kg material 6.1
2.0
Embodied Energy, MJ/kg 83
28
Embodied Water, L/kg 210
94

Common Calculations

PREN (Pitting Resistance) 44
11
Resilience: Ultimate (Unit Rupture Work), MJ/m3 270
83
Resilience: Unit (Modulus of Resilience), kJ/m3 270
100
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 24
25
Strength to Weight: Axial, points 25
15
Strength to Weight: Bending, points 22
16
Thermal Diffusivity, mm2/s 3.3
6.7
Thermal Shock Resistance, points 16
15

Alloy Composition

Carbon (C), % 0 to 0.030
0 to 0.080
Chromium (Cr), % 22 to 24
10.5 to 11.7
Iron (Fe), % 41.7 to 48.8
84.9 to 89.5
Manganese (Mn), % 0 to 1.0
0 to 1.0
Molybdenum (Mo), % 5.0 to 6.0
0
Nickel (Ni), % 24 to 26
0 to 0.5
Nitrogen (N), % 0.17 to 0.22
0
Phosphorus (P), % 0 to 0.030
0 to 0.045
Silicon (Si), % 0 to 1.0
0 to 1.0
Sulfur (S), % 0 to 0.010
0 to 0.030
Titanium (Ti), % 0
0 to 0.75