S32053 Stainless Steel vs. AWS E310H

Both S32053 stainless steel and AWS E310H are iron alloys. They have a moderately high 91% of their average alloy composition in common. There are 25 material properties with values for both materials. Properties with values for just one material (10, in this case) are not shown.

For each property being compared, the top bar is S32053 stainless steel and the bottom bar is AWS E310H.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 210
200
Elongation at Break, % 46
11
Poisson's Ratio 0.28
0.27
Shear Modulus, GPa 80
79
Tensile Strength: Ultimate (UTS), MPa 730
690

Thermal Properties

Latent Heat of Fusion, J/g 310
300
Melting Completion (Liquidus), °C 1450
1400
Melting Onset (Solidus), °C 1400
1350
Specific Heat Capacity, J/kg-K 470
480
Thermal Conductivity, W/m-K 13
14
Thermal Expansion, µm/m-K 16
14

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 1.8
2.1
Electrical Conductivity: Equal Weight (Specific), % IACS 2.0
2.4

Otherwise Unclassified Properties

Base Metal Price, % relative 33
26
Density, g/cm3 8.1
7.9
Embodied Carbon, kg CO2/kg material 6.1
4.6
Embodied Energy, MJ/kg 83
65
Embodied Water, L/kg 210
200

Common Calculations

PREN (Pitting Resistance) 44
28
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 24
25
Strength to Weight: Axial, points 25
25
Strength to Weight: Bending, points 22
22
Thermal Diffusivity, mm2/s 3.3
3.8
Thermal Shock Resistance, points 16
17

Alloy Composition

Carbon (C), % 0 to 0.030
0.35 to 0.45
Chromium (Cr), % 22 to 24
25 to 28
Copper (Cu), % 0
0 to 0.75
Iron (Fe), % 41.7 to 48.8
44.2 to 53.7
Manganese (Mn), % 0 to 1.0
1.0 to 2.5
Molybdenum (Mo), % 5.0 to 6.0
0 to 0.75
Nickel (Ni), % 24 to 26
20 to 22.5
Nitrogen (N), % 0.17 to 0.22
0
Phosphorus (P), % 0 to 0.030
0 to 0.030
Silicon (Si), % 0 to 1.0
0 to 0.75
Sulfur (S), % 0 to 0.010
0 to 0.030