MakeItFrom.com
Menu (ESC)

S32053 Stainless Steel vs. AWS E347

Both S32053 stainless steel and AWS E347 are iron alloys. They have 76% of their average alloy composition in common. There are 25 material properties with values for both materials. Properties with values for just one material (10, in this case) are not shown.

For each property being compared, the top bar is S32053 stainless steel and the bottom bar is AWS E347.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 210
200
Elongation at Break, % 46
34
Poisson's Ratio 0.28
0.28
Shear Modulus, GPa 80
77
Tensile Strength: Ultimate (UTS), MPa 730
580

Thermal Properties

Latent Heat of Fusion, J/g 310
290
Melting Completion (Liquidus), °C 1450
1430
Melting Onset (Solidus), °C 1400
1380
Specific Heat Capacity, J/kg-K 470
480
Thermal Conductivity, W/m-K 13
16
Thermal Expansion, µm/m-K 16
14

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 1.8
2.1
Electrical Conductivity: Equal Weight (Specific), % IACS 2.0
2.4

Otherwise Unclassified Properties

Base Metal Price, % relative 33
19
Density, g/cm3 8.1
7.8
Embodied Carbon, kg CO2/kg material 6.1
3.7
Embodied Energy, MJ/kg 83
53
Embodied Water, L/kg 210
150

Common Calculations

PREN (Pitting Resistance) 44
21
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 24
25
Strength to Weight: Axial, points 25
21
Strength to Weight: Bending, points 22
20
Thermal Diffusivity, mm2/s 3.3
4.2
Thermal Shock Resistance, points 16
15

Alloy Composition

Carbon (C), % 0 to 0.030
0 to 0.080
Chromium (Cr), % 22 to 24
18 to 21
Copper (Cu), % 0
0 to 0.75
Iron (Fe), % 41.7 to 48.8
61.9 to 72.5
Manganese (Mn), % 0 to 1.0
0.5 to 2.5
Molybdenum (Mo), % 5.0 to 6.0
0 to 0.75
Nickel (Ni), % 24 to 26
9.0 to 11
Niobium (Nb), % 0
0 to 1.0
Nitrogen (N), % 0.17 to 0.22
0
Phosphorus (P), % 0 to 0.030
0 to 0.040
Silicon (Si), % 0 to 1.0
0 to 1.0
Sulfur (S), % 0 to 0.010
0 to 0.030