S32053 stainless steel belongs to the iron alloys classification, while AWS ERNiCr-3 belongs to the nickel alloys. They have 47% of their average alloy composition in common. There are 20 material properties with values for both materials. Properties with values for just one material (15, in this case) are not shown.

For each property being compared, the top bar is S32053 stainless steel and the bottom bar is AWS ERNiCr-3.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 210
190
Elongation at Break, % 46
34
Poisson's Ratio 0.28
0.29
Shear Modulus, GPa 80
75
Tensile Strength: Ultimate (UTS), MPa 730
630

Thermal Properties

Latent Heat of Fusion, J/g 310
320
Melting Completion (Liquidus), °C 1450
1380
Melting Onset (Solidus), °C 1400
1330
Specific Heat Capacity, J/kg-K 470
460
Thermal Expansion, µm/m-K 16
13

Otherwise Unclassified Properties

Base Metal Price, % relative 33
70
Density, g/cm3 8.1
8.4
Embodied Carbon, kg CO2/kg material 6.1
11
Embodied Energy, MJ/kg 83
160
Embodied Water, L/kg 210
280

Common Calculations

Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 24
23
Strength to Weight: Axial, points 25
21
Strength to Weight: Bending, points 22
19
Thermal Shock Resistance, points 16
18

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 460
Carbon (C), % 0 to 0.030
0 to 0.1
Chromium (Cr), % 22 to 24
18 to 22
Cobalt (Co), % 0
0 to 0.12
Copper (Cu), % 0
0 to 0.5
Iron (Fe), % 41.7 to 48.8
0 to 3.0
Manganese (Mn), % 0 to 1.0
2.5 to 3.5
Molybdenum (Mo), % 5.0 to 6.0
0
Nickel (Ni), % 24 to 26
67 to 77.5
Niobium (Nb), % 0
2.0 to 3.0
Nitrogen (N), % 0.17 to 0.22
0
Phosphorus (P), % 0 to 0.030
0 to 0.030
Silicon (Si), % 0 to 1.0
0 to 0.5
Sulfur (S), % 0 to 0.010
0 to 0.015
Titanium (Ti), % 0
0 to 0.75
Residuals, % 0
0 to 0.5