S32053 Stainless Steel vs. EN 1.0214 Steel

Both S32053 stainless steel and EN 1.0214 steel are iron alloys. They have 46% of their average alloy composition in common. There are 32 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown.

For each property being compared, the top bar is S32053 stainless steel and the bottom bar is EN 1.0214 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 190
97 to 130
Elastic (Young's, Tensile) Modulus, GPa 210
190
Elongation at Break, % 46
12 to 31
Fatigue Strength, MPa 310
160 to 250
Poisson's Ratio 0.28
0.29
Reduction in Area, % 56
66 to 80
Shear Modulus, GPa 80
73
Shear Strength, MPa 510
250 to 290
Tensile Strength: Ultimate (UTS), MPa 730
330 to 460
Tensile Strength: Yield (Proof), MPa 330
210 to 360

Thermal Properties

Latent Heat of Fusion, J/g 310
250
Maximum Temperature: Mechanical, °C 1100
400
Melting Completion (Liquidus), °C 1450
1470
Melting Onset (Solidus), °C 1400
1420
Specific Heat Capacity, J/kg-K 470
470
Thermal Conductivity, W/m-K 13
53
Thermal Expansion, µm/m-K 16
12

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 1.8
6.9
Electrical Conductivity: Equal Weight (Specific), % IACS 2.0
7.9

Otherwise Unclassified Properties

Base Metal Price, % relative 33
1.8
Density, g/cm3 8.1
7.9
Embodied Carbon, kg CO2/kg material 6.1
1.4
Embodied Energy, MJ/kg 83
18
Embodied Water, L/kg 210
46

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 270
34 to 130
Resilience: Unit (Modulus of Resilience), kJ/m3 270
120 to 340
Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 24
24
Strength to Weight: Axial, points 25
12 to 16
Strength to Weight: Bending, points 22
14 to 17
Thermal Diffusivity, mm2/s 3.3
14
Thermal Shock Resistance, points 16
11 to 14

Alloy Composition

Aluminum (Al), % 0
0.020 to 0.060
Carbon (C), % 0 to 0.030
0.080 to 0.12
Chromium (Cr), % 22 to 24
0
Iron (Fe), % 41.7 to 48.8
99.17 to 99.6
Manganese (Mn), % 0 to 1.0
0.3 to 0.5
Molybdenum (Mo), % 5.0 to 6.0
0
Nickel (Ni), % 24 to 26
0
Nitrogen (N), % 0.17 to 0.22
0
Phosphorus (P), % 0 to 0.030
0 to 0.025
Silicon (Si), % 0 to 1.0
0 to 0.1
Sulfur (S), % 0 to 0.010
0 to 0.025