MakeItFrom.com
Menu (ESC)

S32053 Stainless Steel vs. EN 1.0535 Steel

Both S32053 stainless steel and EN 1.0535 steel are iron alloys. They have 46% of their average alloy composition in common. There are 31 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown.

For each property being compared, the top bar is S32053 stainless steel and the bottom bar is EN 1.0535 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 190
200
Elastic (Young's, Tensile) Modulus, GPa 210
190
Elongation at Break, % 46
12
Fatigue Strength, MPa 310
210
Poisson's Ratio 0.28
0.29
Shear Modulus, GPa 80
72
Shear Strength, MPa 510
420
Tensile Strength: Ultimate (UTS), MPa 730
690
Tensile Strength: Yield (Proof), MPa 330
340

Thermal Properties

Latent Heat of Fusion, J/g 310
250
Maximum Temperature: Mechanical, °C 1100
400
Melting Completion (Liquidus), °C 1450
1460
Melting Onset (Solidus), °C 1400
1410
Specific Heat Capacity, J/kg-K 470
470
Thermal Conductivity, W/m-K 13
48
Thermal Expansion, µm/m-K 16
12

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 1.8
7.2
Electrical Conductivity: Equal Weight (Specific), % IACS 2.0
8.3

Otherwise Unclassified Properties

Base Metal Price, % relative 33
2.1
Density, g/cm3 8.1
7.8
Embodied Carbon, kg CO2/kg material 6.1
1.4
Embodied Energy, MJ/kg 83
19
Embodied Water, L/kg 210
47

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 270
69
Resilience: Unit (Modulus of Resilience), kJ/m3 270
310
Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 24
24
Strength to Weight: Axial, points 25
25
Strength to Weight: Bending, points 22
22
Thermal Diffusivity, mm2/s 3.3
13
Thermal Shock Resistance, points 16
22

Alloy Composition

Carbon (C), % 0 to 0.030
0.52 to 0.6
Chromium (Cr), % 22 to 24
0 to 0.4
Iron (Fe), % 41.7 to 48.8
97.1 to 98.9
Manganese (Mn), % 0 to 1.0
0.6 to 0.9
Molybdenum (Mo), % 5.0 to 6.0
0 to 0.1
Nickel (Ni), % 24 to 26
0 to 0.4
Nitrogen (N), % 0.17 to 0.22
0
Phosphorus (P), % 0 to 0.030
0 to 0.045
Silicon (Si), % 0 to 1.0
0 to 0.4
Sulfur (S), % 0 to 0.010
0 to 0.045