S32053 Stainless Steel vs. EN 1.1181 Steel

Both S32053 stainless steel and EN 1.1181 steel are iron alloys. They have 46% of their average alloy composition in common. There are 31 material properties with values for both materials. Properties with values for just one material (5, in this case) are not shown.

For each property being compared, the top bar is S32053 stainless steel and the bottom bar is EN 1.1181 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 190
160 to 180
Elastic (Young's, Tensile) Modulus, GPa 210
190
Elongation at Break, % 46
19 to 20
Fatigue Strength, MPa 310
190 to 260
Poisson's Ratio 0.28
0.29
Shear Modulus, GPa 80
73
Shear Strength, MPa 510
350 to 390
Tensile Strength: Ultimate (UTS), MPa 730
560 to 620
Tensile Strength: Yield (Proof), MPa 330
280 to 380

Thermal Properties

Latent Heat of Fusion, J/g 310
250
Maximum Temperature: Mechanical, °C 1100
400
Melting Completion (Liquidus), °C 1450
1460
Melting Onset (Solidus), °C 1400
1420
Specific Heat Capacity, J/kg-K 470
470
Thermal Conductivity, W/m-K 13
42
Thermal Expansion, µm/m-K 16
11

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 1.8
7.2
Electrical Conductivity: Equal Weight (Specific), % IACS 2.0
8.3

Otherwise Unclassified Properties

Base Metal Price, % relative 33
2.1
Density, g/cm3 8.1
7.8
Embodied Carbon, kg CO2/kg material 6.1
1.4
Embodied Energy, MJ/kg 83
19
Embodied Water, L/kg 210
47

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 270
90 to 110
Resilience: Unit (Modulus of Resilience), kJ/m3 270
210 to 380
Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 24
24
Strength to Weight: Axial, points 25
20 to 22
Strength to Weight: Bending, points 22
19 to 21
Thermal Diffusivity, mm2/s 3.3
11
Thermal Shock Resistance, points 16
19 to 21

Alloy Composition

Carbon (C), % 0 to 0.030
0.32 to 0.39
Chromium (Cr), % 22 to 24
0 to 0.4
Iron (Fe), % 41.7 to 48.8
97.4 to 99.18
Manganese (Mn), % 0 to 1.0
0.5 to 0.8
Molybdenum (Mo), % 5.0 to 6.0
0 to 0.1
Nickel (Ni), % 24 to 26
0 to 0.4
Nitrogen (N), % 0.17 to 0.22
0
Phosphorus (P), % 0 to 0.030
0 to 0.035
Silicon (Si), % 0 to 1.0
0 to 0.4
Sulfur (S), % 0 to 0.010
0 to 0.035