S32053 Stainless Steel vs. EN 1.3523 Steel

Both S32053 stainless steel and EN 1.3523 steel are iron alloys. They have 47% of their average alloy composition in common. There are 25 material properties with values for both materials. Properties with values for just one material (10, in this case) are not shown.

For each property being compared, the top bar is S32053 stainless steel and the bottom bar is EN 1.3523 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 190
160 to 220
Elastic (Young's, Tensile) Modulus, GPa 210
190
Poisson's Ratio 0.28
0.29
Shear Modulus, GPa 80
73
Tensile Strength: Ultimate (UTS), MPa 730
520 to 1460

Thermal Properties

Latent Heat of Fusion, J/g 310
250
Maximum Temperature: Mechanical, °C 1100
420
Melting Completion (Liquidus), °C 1450
1460
Melting Onset (Solidus), °C 1400
1420
Specific Heat Capacity, J/kg-K 470
470
Thermal Conductivity, W/m-K 13
46
Thermal Expansion, µm/m-K 16
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 1.8
7.3
Electrical Conductivity: Equal Weight (Specific), % IACS 2.0
8.4

Otherwise Unclassified Properties

Base Metal Price, % relative 33
2.3
Density, g/cm3 8.1
7.8
Embodied Carbon, kg CO2/kg material 6.1
1.5
Embodied Energy, MJ/kg 83
19
Embodied Water, L/kg 210
53

Common Calculations

Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 24
24
Strength to Weight: Axial, points 25
19 to 52
Strength to Weight: Bending, points 22
18 to 36
Thermal Diffusivity, mm2/s 3.3
12
Thermal Shock Resistance, points 16
15 to 42

Alloy Composition

Aluminum (Al), % 0
0 to 0.050
Carbon (C), % 0 to 0.030
0.17 to 0.22
Chromium (Cr), % 22 to 24
1.0 to 1.3
Copper (Cu), % 0
0 to 0.3
Iron (Fe), % 41.7 to 48.8
96.5 to 97.9
Manganese (Mn), % 0 to 1.0
1.1 to 1.4
Molybdenum (Mo), % 5.0 to 6.0
0
Nickel (Ni), % 24 to 26
0
Nitrogen (N), % 0.17 to 0.22
0
Oxygen (O), % 0
0 to 0.0020
Phosphorus (P), % 0 to 0.030
0 to 0.025
Silicon (Si), % 0 to 1.0
0 to 0.4
Sulfur (S), % 0 to 0.010
0 to 0.030