S32053 Stainless Steel vs. EN 1.3536 Steel

Both S32053 stainless steel and EN 1.3536 steel are iron alloys. They have 48% of their average alloy composition in common. There are 26 material properties with values for both materials. Properties with values for just one material (9, in this case) are not shown.

For each property being compared, the top bar is S32053 stainless steel and the bottom bar is EN 1.3536 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 190
200
Elastic (Young's, Tensile) Modulus, GPa 210
190
Poisson's Ratio 0.28
0.29
Shear Modulus, GPa 80
73
Tensile Strength: Ultimate (UTS), MPa 730
660

Thermal Properties

Latent Heat of Fusion, J/g 310
250
Maximum Temperature: Mechanical, °C 1100
440
Melting Completion (Liquidus), °C 1450
1450
Melting Onset (Solidus), °C 1400
1410
Specific Heat Capacity, J/kg-K 470
470
Thermal Conductivity, W/m-K 13
41
Thermal Expansion, µm/m-K 16
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 1.8
7.4
Electrical Conductivity: Equal Weight (Specific), % IACS 2.0
8.5

Otherwise Unclassified Properties

Base Metal Price, % relative 33
2.9
Density, g/cm3 8.1
7.8
Embodied Carbon, kg CO2/kg material 6.1
1.6
Embodied Energy, MJ/kg 83
21
Embodied Water, L/kg 210
55

Common Calculations

PREN (Pitting Resistance) 44
2.8
Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 24
24
Strength to Weight: Axial, points 25
23
Strength to Weight: Bending, points 22
22
Thermal Diffusivity, mm2/s 3.3
11
Thermal Shock Resistance, points 16
19

Alloy Composition

Aluminum (Al), % 0
0 to 0.050
Carbon (C), % 0 to 0.030
0.93 to 1.1
Chromium (Cr), % 22 to 24
1.7 to 2.0
Copper (Cu), % 0
0 to 0.3
Iron (Fe), % 41.7 to 48.8
96 to 97.4
Manganese (Mn), % 0 to 1.0
0.6 to 0.8
Molybdenum (Mo), % 5.0 to 6.0
0.2 to 0.35
Nickel (Ni), % 24 to 26
0
Nitrogen (N), % 0.17 to 0.22
0
Oxygen (O), % 0
0 to 0.0015
Phosphorus (P), % 0 to 0.030
0 to 0.025
Silicon (Si), % 0 to 1.0
0.15 to 0.45
Sulfur (S), % 0 to 0.010
0 to 0.030