S32053 Stainless Steel vs. EN 1.4313 Stainless Steel

Both S32053 stainless steel and EN 1.4313 stainless steel are iron alloys. They have 64% of their average alloy composition in common. There are 32 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown.

For each property being compared, the top bar is S32053 stainless steel and the bottom bar is EN 1.4313 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 210
200
Elongation at Break, % 46
12 to 17
Fatigue Strength, MPa 310
340 to 510
Poisson's Ratio 0.28
0.28
Shear Modulus, GPa 80
76
Shear Strength, MPa 510
460 to 600
Tensile Strength: Ultimate (UTS), MPa 730
750 to 1000
Tensile Strength: Yield (Proof), MPa 330
580 to 910

Thermal Properties

Latent Heat of Fusion, J/g 310
280
Maximum Temperature: Corrosion, °C 440
390
Maximum Temperature: Mechanical, °C 1100
780
Melting Completion (Liquidus), °C 1450
1450
Melting Onset (Solidus), °C 1400
1400
Specific Heat Capacity, J/kg-K 470
480
Thermal Conductivity, W/m-K 13
25
Thermal Expansion, µm/m-K 16
10

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 1.8
2.9
Electrical Conductivity: Equal Weight (Specific), % IACS 2.0
3.3

Otherwise Unclassified Properties

Base Metal Price, % relative 33
10
Density, g/cm3 8.1
7.8
Embodied Carbon, kg CO2/kg material 6.1
2.4
Embodied Energy, MJ/kg 83
34
Embodied Water, L/kg 210
110

Common Calculations

PREN (Pitting Resistance) 44
15
Resilience: Ultimate (Unit Rupture Work), MJ/m3 270
110 to 150
Resilience: Unit (Modulus of Resilience), kJ/m3 270
870 to 2100
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 24
25
Strength to Weight: Axial, points 25
27 to 36
Strength to Weight: Bending, points 22
23 to 28
Thermal Diffusivity, mm2/s 3.3
6.7
Thermal Shock Resistance, points 16
27 to 36

Alloy Composition

Carbon (C), % 0 to 0.030
0 to 0.050
Chromium (Cr), % 22 to 24
12 to 14
Iron (Fe), % 41.7 to 48.8
78.5 to 84.2
Manganese (Mn), % 0 to 1.0
0 to 1.5
Molybdenum (Mo), % 5.0 to 6.0
0.3 to 0.7
Nickel (Ni), % 24 to 26
3.5 to 4.5
Nitrogen (N), % 0.17 to 0.22
0 to 0.020
Phosphorus (P), % 0 to 0.030
0 to 0.040
Silicon (Si), % 0 to 1.0
0 to 0.7
Sulfur (S), % 0 to 0.010
0 to 0.015