S32053 Stainless Steel vs. EN 1.5514 Steel

Both S32053 stainless steel and EN 1.5514 steel are iron alloys. They have 46% of their average alloy composition in common. There are 26 material properties with values for both materials. Properties with values for just one material (9, in this case) are not shown.

For each property being compared, the top bar is S32053 stainless steel and the bottom bar is EN 1.5514 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 190
140 to 170
Elastic (Young's, Tensile) Modulus, GPa 210
190
Poisson's Ratio 0.28
0.29
Reduction in Area, % 56
64 to 69
Shear Modulus, GPa 80
73
Tensile Strength: Ultimate (UTS), MPa 730
470 to 1680

Thermal Properties

Latent Heat of Fusion, J/g 310
250
Maximum Temperature: Mechanical, °C 1100
400
Melting Completion (Liquidus), °C 1450
1460
Melting Onset (Solidus), °C 1400
1420
Specific Heat Capacity, J/kg-K 470
470
Thermal Conductivity, W/m-K 13
49
Thermal Expansion, µm/m-K 16
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 1.8
7.1
Electrical Conductivity: Equal Weight (Specific), % IACS 2.0
8.2

Otherwise Unclassified Properties

Base Metal Price, % relative 33
1.9
Density, g/cm3 8.1
7.8
Embodied Carbon, kg CO2/kg material 6.1
1.4
Embodied Energy, MJ/kg 83
19
Embodied Water, L/kg 210
47

Common Calculations

Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 24
24
Strength to Weight: Axial, points 25
17 to 60
Strength to Weight: Bending, points 22
17 to 40
Thermal Diffusivity, mm2/s 3.3
13
Thermal Shock Resistance, points 16
14 to 50

Alloy Composition

Boron (B), % 0
0.00080 to 0.0050
Carbon (C), % 0 to 0.030
0.3 to 0.35
Chromium (Cr), % 22 to 24
0 to 0.3
Copper (Cu), % 0
0 to 0.25
Iron (Fe), % 41.7 to 48.8
97.8 to 99.099
Manganese (Mn), % 0 to 1.0
0.6 to 0.9
Molybdenum (Mo), % 5.0 to 6.0
0
Nickel (Ni), % 24 to 26
0
Nitrogen (N), % 0.17 to 0.22
0
Phosphorus (P), % 0 to 0.030
0 to 0.025
Silicon (Si), % 0 to 1.0
0 to 0.3
Sulfur (S), % 0 to 0.010
0 to 0.025