MakeItFrom.com
Menu (ESC)

S32053 Stainless Steel vs. EN 1.6220 Steel

Both S32053 stainless steel and EN 1.6220 steel are iron alloys. They have 46% of their average alloy composition in common. There are 30 material properties with values for both materials. Properties with values for just one material (6, in this case) are not shown.

For each property being compared, the top bar is S32053 stainless steel and the bottom bar is EN 1.6220 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 190
170
Elastic (Young's, Tensile) Modulus, GPa 210
190
Elongation at Break, % 46
23 to 25
Fatigue Strength, MPa 310
240 to 250
Poisson's Ratio 0.28
0.29
Shear Modulus, GPa 80
73
Tensile Strength: Ultimate (UTS), MPa 730
550 to 580
Tensile Strength: Yield (Proof), MPa 330
340

Thermal Properties

Latent Heat of Fusion, J/g 310
250
Maximum Temperature: Mechanical, °C 1100
400
Melting Completion (Liquidus), °C 1450
1460
Melting Onset (Solidus), °C 1400
1420
Specific Heat Capacity, J/kg-K 470
470
Thermal Conductivity, W/m-K 13
52
Thermal Expansion, µm/m-K 16
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 1.8
7.3
Electrical Conductivity: Equal Weight (Specific), % IACS 2.0
8.4

Otherwise Unclassified Properties

Base Metal Price, % relative 33
2.1
Density, g/cm3 8.1
7.8
Embodied Carbon, kg CO2/kg material 6.1
1.5
Embodied Energy, MJ/kg 83
19
Embodied Water, L/kg 210
48

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 270
110 to 120
Resilience: Unit (Modulus of Resilience), kJ/m3 270
300 to 310
Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 24
24
Strength to Weight: Axial, points 25
19 to 20
Strength to Weight: Bending, points 22
19 to 20
Thermal Diffusivity, mm2/s 3.3
14
Thermal Shock Resistance, points 16
16 to 17

Alloy Composition

Carbon (C), % 0 to 0.030
0.17 to 0.23
Chromium (Cr), % 22 to 24
0
Iron (Fe), % 41.7 to 48.8
96.7 to 98.8
Manganese (Mn), % 0 to 1.0
1.0 to 1.6
Molybdenum (Mo), % 5.0 to 6.0
0
Nickel (Ni), % 24 to 26
0 to 0.8
Nitrogen (N), % 0.17 to 0.22
0
Phosphorus (P), % 0 to 0.030
0 to 0.020
Silicon (Si), % 0 to 1.0
0 to 0.6
Sulfur (S), % 0 to 0.010
0 to 0.030