S32053 Stainless Steel vs. EN 2.4816 Nickel

S32053 stainless steel belongs to the iron alloys classification, while EN 2.4816 nickel belongs to the nickel alloys. They have 49% of their average alloy composition in common. There are 31 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown.

For each property being compared, the top bar is S32053 stainless steel and the bottom bar is EN 2.4816 nickel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 190
170
Elastic (Young's, Tensile) Modulus, GPa 210
190
Elongation at Break, % 46
34
Fatigue Strength, MPa 310
200
Poisson's Ratio 0.28
0.29
Shear Modulus, GPa 80
74
Shear Strength, MPa 510
470
Tensile Strength: Ultimate (UTS), MPa 730
700
Tensile Strength: Yield (Proof), MPa 330
270

Thermal Properties

Latent Heat of Fusion, J/g 310
310
Maximum Temperature: Mechanical, °C 1100
1150
Melting Completion (Liquidus), °C 1450
1370
Melting Onset (Solidus), °C 1400
1320
Specific Heat Capacity, J/kg-K 470
460
Thermal Conductivity, W/m-K 13
15
Thermal Expansion, µm/m-K 16
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 1.8
1.7
Electrical Conductivity: Equal Weight (Specific), % IACS 2.0
1.8

Otherwise Unclassified Properties

Base Metal Price, % relative 33
55
Density, g/cm3 8.1
8.5
Embodied Carbon, kg CO2/kg material 6.1
9.0
Embodied Energy, MJ/kg 83
130
Embodied Water, L/kg 210
260

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 270
190
Resilience: Unit (Modulus of Resilience), kJ/m3 270
190
Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 24
23
Strength to Weight: Axial, points 25
23
Strength to Weight: Bending, points 22
21
Thermal Diffusivity, mm2/s 3.3
3.8
Thermal Shock Resistance, points 16
20

Alloy Composition

Aluminum (Al), % 0
0 to 0.3
Carbon (C), % 0 to 0.030
0.050 to 0.1
Chromium (Cr), % 22 to 24
14 to 17
Copper (Cu), % 0
0 to 0.5
Iron (Fe), % 41.7 to 48.8
6.0 to 10
Manganese (Mn), % 0 to 1.0
0 to 1.0
Molybdenum (Mo), % 5.0 to 6.0
0
Nickel (Ni), % 24 to 26
72 to 80
Nitrogen (N), % 0.17 to 0.22
0
Phosphorus (P), % 0 to 0.030
0 to 0.020
Silicon (Si), % 0 to 1.0
0 to 0.5
Sulfur (S), % 0 to 0.010
0 to 0.015
Titanium (Ti), % 0
0 to 0.3