S32053 Stainless Steel vs. EN 2.4889 Nickel

S32053 stainless steel belongs to the iron alloys classification, while EN 2.4889 nickel belongs to the nickel alloys. They have 72% of their average alloy composition in common. There are 32 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown.

For each property being compared, the top bar is S32053 stainless steel and the bottom bar is EN 2.4889 nickel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 190
190
Elastic (Young's, Tensile) Modulus, GPa 210
200
Elongation at Break, % 46
39
Fatigue Strength, MPa 310
210
Poisson's Ratio 0.28
0.28
Shear Modulus, GPa 80
77
Shear Strength, MPa 510
490
Tensile Strength: Ultimate (UTS), MPa 730
720
Tensile Strength: Yield (Proof), MPa 330
270

Thermal Properties

Latent Heat of Fusion, J/g 310
350
Maximum Temperature: Mechanical, °C 1100
1200
Melting Completion (Liquidus), °C 1450
1350
Melting Onset (Solidus), °C 1400
1300
Specific Heat Capacity, J/kg-K 470
480
Thermal Conductivity, W/m-K 13
13
Thermal Expansion, µm/m-K 16
14

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 1.8
1.5
Electrical Conductivity: Equal Weight (Specific), % IACS 2.0
1.6

Otherwise Unclassified Properties

Base Metal Price, % relative 33
42
Density, g/cm3 8.1
8.0
Embodied Carbon, kg CO2/kg material 6.1
6.9
Embodied Energy, MJ/kg 83
98
Embodied Water, L/kg 210
250

Common Calculations

PREN (Pitting Resistance) 44
28
Resilience: Ultimate (Unit Rupture Work), MJ/m3 270
220
Resilience: Unit (Modulus of Resilience), kJ/m3 270
180
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 24
24
Strength to Weight: Axial, points 25
25
Strength to Weight: Bending, points 22
22
Thermal Diffusivity, mm2/s 3.3
3.4
Thermal Shock Resistance, points 16
19

Alloy Composition

Carbon (C), % 0 to 0.030
0.050 to 0.12
Cerium (Ce), % 0
0.030 to 0.090
Chromium (Cr), % 22 to 24
26 to 29
Copper (Cu), % 0
0 to 0.3
Iron (Fe), % 41.7 to 48.8
21 to 25
Manganese (Mn), % 0 to 1.0
0 to 1.0
Molybdenum (Mo), % 5.0 to 6.0
0
Nickel (Ni), % 24 to 26
45 to 50.4
Nitrogen (N), % 0.17 to 0.22
0
Phosphorus (P), % 0 to 0.030
0 to 0.020
Silicon (Si), % 0 to 1.0
2.5 to 3.0
Sulfur (S), % 0 to 0.010
0 to 0.010