S32053 Stainless Steel vs. Nickel Beryllium 360

S32053 stainless steel belongs to the iron alloys classification, while nickel beryllium 360 belongs to the nickel alloys. There are 24 material properties with values for both materials. Properties with values for just one material (11, in this case) are not shown.

For each property being compared, the top bar is S32053 stainless steel and the bottom bar is nickel beryllium 360.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 210
200
Elongation at Break, % 46
1.0 to 30
Fatigue Strength, MPa 310
260 to 710
Poisson's Ratio 0.28
0.3
Shear Modulus, GPa 80
77
Shear Strength, MPa 510
510 to 1100
Tensile Strength: Ultimate (UTS), MPa 730
780 to 1860
Tensile Strength: Yield (Proof), MPa 330
380 to 1590

Thermal Properties

Melting Completion (Liquidus), °C 1450
1330
Melting Onset (Solidus), °C 1400
1200
Specific Heat Capacity, J/kg-K 470
460
Thermal Conductivity, W/m-K 13
48
Thermal Expansion, µm/m-K 16
14

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 1.8
5.0
Electrical Conductivity: Equal Weight (Specific), % IACS 2.0
5.4

Otherwise Unclassified Properties

Density, g/cm3 8.1
8.3

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 270
12 to 190
Resilience: Unit (Modulus of Resilience), kJ/m3 270
360 to 3440
Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 24
24
Strength to Weight: Axial, points 25
26 to 62
Strength to Weight: Bending, points 22
23 to 41
Thermal Diffusivity, mm2/s 3.3
13
Thermal Shock Resistance, points 16
19 to 46