S32053 Stainless Steel vs. SAE-AISI T15 Steel

Both S32053 stainless steel and SAE-AISI T15 steel are iron alloys. They have 51% of their average alloy composition in common. There are 22 material properties with values for both materials. Properties with values for just one material (13, in this case) are not shown.

For each property being compared, the top bar is S32053 stainless steel and the bottom bar is SAE-AISI T15 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 210
200
Poisson's Ratio 0.28
0.29
Shear Modulus, GPa 80
76
Tensile Strength: Ultimate (UTS), MPa 730
830 to 2240

Thermal Properties

Latent Heat of Fusion, J/g 310
250
Melting Completion (Liquidus), °C 1450
1690
Melting Onset (Solidus), °C 1400
1640
Specific Heat Capacity, J/kg-K 470
430
Thermal Conductivity, W/m-K 13
21
Thermal Expansion, µm/m-K 16
12

Otherwise Unclassified Properties

Base Metal Price, % relative 33
43
Density, g/cm3 8.1
8.7
Embodied Carbon, kg CO2/kg material 6.1
16
Embodied Energy, MJ/kg 83
250
Embodied Water, L/kg 210
140

Common Calculations

PREN (Pitting Resistance) 44
27
Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 24
22
Strength to Weight: Axial, points 25
26 to 71
Strength to Weight: Bending, points 22
22 to 43
Thermal Diffusivity, mm2/s 3.3
5.6
Thermal Shock Resistance, points 16
26 to 70

Alloy Composition

Carbon (C), % 0 to 0.030
1.5 to 1.6
Chromium (Cr), % 22 to 24
3.8 to 5.0
Cobalt (Co), % 0
4.8 to 5.3
Copper (Cu), % 0
0 to 0.25
Iron (Fe), % 41.7 to 48.8
67.5 to 73.5
Manganese (Mn), % 0 to 1.0
0.15 to 0.4
Molybdenum (Mo), % 5.0 to 6.0
0 to 1.0
Nickel (Ni), % 24 to 26
0 to 0.3
Nitrogen (N), % 0.17 to 0.22
0
Phosphorus (P), % 0 to 0.030
0 to 0.030
Silicon (Si), % 0 to 1.0
0.15 to 0.4
Sulfur (S), % 0 to 0.010
0 to 0.030
Tungsten (W), % 0
11.8 to 13
Vanadium (V), % 0
4.5 to 5.3