MakeItFrom.com
Menu (ESC)

S32053 Stainless Steel vs. N06200 Nickel

S32053 stainless steel belongs to the iron alloys classification, while N06200 nickel belongs to the nickel alloys. They have 55% of their average alloy composition in common. There are 30 material properties with values for both materials. Properties with values for just one material (5, in this case) are not shown.

For each property being compared, the top bar is S32053 stainless steel and the bottom bar is N06200 nickel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 210
220
Elongation at Break, % 46
51
Fatigue Strength, MPa 310
290
Poisson's Ratio 0.28
0.29
Shear Modulus, GPa 80
84
Shear Strength, MPa 510
560
Tensile Strength: Ultimate (UTS), MPa 730
780
Tensile Strength: Yield (Proof), MPa 330
320

Thermal Properties

Latent Heat of Fusion, J/g 310
330
Maximum Temperature: Mechanical, °C 1100
990
Melting Completion (Liquidus), °C 1450
1500
Melting Onset (Solidus), °C 1400
1450
Specific Heat Capacity, J/kg-K 470
430
Thermal Conductivity, W/m-K 13
9.1
Thermal Expansion, µm/m-K 16
12

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 1.8
1.3
Electrical Conductivity: Equal Weight (Specific), % IACS 2.0
1.4

Otherwise Unclassified Properties

Base Metal Price, % relative 33
65
Density, g/cm3 8.1
8.7
Embodied Carbon, kg CO2/kg material 6.1
12
Embodied Energy, MJ/kg 83
160
Embodied Water, L/kg 210
310

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 270
320
Resilience: Unit (Modulus of Resilience), kJ/m3 270
240
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 24
23
Strength to Weight: Axial, points 25
25
Strength to Weight: Bending, points 22
22
Thermal Diffusivity, mm2/s 3.3
2.4
Thermal Shock Resistance, points 16
21

Alloy Composition

Aluminum (Al), % 0
0 to 0.5
Carbon (C), % 0 to 0.030
0 to 0.010
Chromium (Cr), % 22 to 24
22 to 24
Cobalt (Co), % 0
0 to 2.0
Copper (Cu), % 0
1.3 to 1.9
Iron (Fe), % 41.7 to 48.8
0 to 3.0
Manganese (Mn), % 0 to 1.0
0 to 0.010
Molybdenum (Mo), % 5.0 to 6.0
15 to 17
Nickel (Ni), % 24 to 26
51 to 61.7
Nitrogen (N), % 0.17 to 0.22
0
Phosphorus (P), % 0 to 0.030
0 to 0.025
Silicon (Si), % 0 to 1.0
0 to 0.080
Sulfur (S), % 0 to 0.010
0 to 0.010