S32053 Stainless Steel vs. S45500 Stainless Steel

Both S32053 stainless steel and S45500 stainless steel are iron alloys. They have 66% of their average alloy composition in common. There are 29 material properties with values for both materials. Properties with values for just one material (7, in this case) are not shown.

For each property being compared, the top bar is S32053 stainless steel and the bottom bar is S45500 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 190
280 to 500
Elastic (Young's, Tensile) Modulus, GPa 210
190
Elongation at Break, % 46
3.4 to 11
Fatigue Strength, MPa 310
570 to 890
Poisson's Ratio 0.28
0.28
Reduction in Area, % 56
34 to 45
Shear Modulus, GPa 80
75
Shear Strength, MPa 510
790 to 1090
Tensile Strength: Ultimate (UTS), MPa 730
1370 to 1850
Tensile Strength: Yield (Proof), MPa 330
1240 to 1700

Thermal Properties

Latent Heat of Fusion, J/g 310
270
Maximum Temperature: Corrosion, °C 440
620
Maximum Temperature: Mechanical, °C 1100
760
Melting Completion (Liquidus), °C 1450
1440
Melting Onset (Solidus), °C 1400
1400
Specific Heat Capacity, J/kg-K 470
470
Thermal Expansion, µm/m-K 16
11

Otherwise Unclassified Properties

Base Metal Price, % relative 33
17
Density, g/cm3 8.1
7.9
Embodied Carbon, kg CO2/kg material 6.1
3.8
Embodied Energy, MJ/kg 83
57
Embodied Water, L/kg 210
120

Common Calculations

PREN (Pitting Resistance) 44
13
Resilience: Ultimate (Unit Rupture Work), MJ/m3 270
45 to 190
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 24
24
Strength to Weight: Axial, points 25
48 to 65
Strength to Weight: Bending, points 22
35 to 42
Thermal Shock Resistance, points 16
48 to 64

Alloy Composition

Carbon (C), % 0 to 0.030
0 to 0.050
Chromium (Cr), % 22 to 24
11 to 12.5
Copper (Cu), % 0
1.5 to 2.5
Iron (Fe), % 41.7 to 48.8
71.5 to 79.2
Manganese (Mn), % 0 to 1.0
0 to 0.5
Molybdenum (Mo), % 5.0 to 6.0
0 to 0.5
Nickel (Ni), % 24 to 26
7.5 to 9.5
Niobium (Nb), % 0
0 to 0.5
Nitrogen (N), % 0.17 to 0.22
0
Phosphorus (P), % 0 to 0.030
0 to 0.040
Silicon (Si), % 0 to 1.0
0 to 0.5
Sulfur (S), % 0 to 0.010
0 to 0.030
Tantalum (Ta), % 0
0 to 0.5
Titanium (Ti), % 0
0.8 to 1.4